二段固相反応法によるLi[Ni_<1/2>Mn_<3/2>]O_4の合成とキャラクタリゼーション(<特集>セラミックスインテグレーション)

概要

論文の詳細を見る
A five-volt lithium insertion material of Li[Ni_<1/2>Mn_<3/2>]O_4, having a spinel-framework structure, was prepared from nickel manganese double hydroxide with LiOH and characterized by XRD, FT-IR, TG, SEM and electrochemical methods. Heating a reaction mixture below 600℃ did not give good results in terms of polarization and cycleability during charge and discharge in lithium nonaqueous cells. Higher heating temperatures gave lower polarization and better cycleability, while rechargeable capacity at 4.75 V vs. Li reduces as heating temperature rises. After several trials, an optimum condition to prepare a five-volt lithium insertion material of Li[Ni_<1/>Mn_<3/2>]O_4 is found to be a two-step solid state reaction, i.e., crystallization at 1000℃ followed by oxidation at 700℃. By this process Li[Ni_<1/2>Mn_<3/2>]O_4 showed an excellent performance in a five-volt nonaqueous lithium cell and also in a three-volt lithium-ion cell with a Li[Li_<1/3>Ti_<5/3>]O_4-negative electrode.
社団法人日本セラミックス協会の論文
2002-05-01