The single crystals of a new quaternary compound ErRh_2B_2C have been obtained as thin plates in an atmosphere of helium by the flux method using molten copper. The single crystals show golden-colored luster and the maximum size obtained is about 1.0 x 1.0 x 0.02 mm^3. This compound belongs to a tetragonal system and seems to be a derivative of ThCr_2Si_2 type; lattice parameter: a=0.36848 (2)nm, c=1.05520(3)nm, V= 1.4327 x 10-^28 m^3 and Z=2. The electrical resistivity parallel to the a-b plane decreases monotonically with decreasing temperature, but no superconductivity is observed down to 1.5K. The residual resistivity ratio, p (273 K) /p (1.5 K), is 1.38. Similar type new compounds of RRh_2B_2C were obtained for R=La-Er (except Eu and Tm) and Y by arc-melting synthetic method.
- 社団法人日本セラミックス協会の論文
- 1996-12-01
著者
-
松本 武彦
金材技研
-
宍戸 統悦
東北大学金属材料研究所
-
福田 承生
東北大学金属材料研究所
-
宍戸 統悦
東北大金研
-
葉 金花
物質研
-
松本 武彦
金材研
-
葉 金花
科学技術庁金属材料技術研究所
-
佐々木 孝彦
東北大学金属材料研究所
-
Fukuda T
Gunma Univ. Gunma Jpn
-
松本 武彦
科学技術庁金属材料技術研究所
関連論文
- 19aPS-4 CeRh_2Si_2の高圧下^Si NMR
- 18pYD-5 URu_2Si_2の高圧下^Si-NMR
- 27aYK-5 URu_2Si_2の高圧下^Si-NMR
- 6a-PS-10 酸化物超伝導体の超伝導転移温度と圧力効果
- 28p-PSA-38 LaSrYCu_2O_6のメスバウアー効果II
- Pr124酸化物の結晶構造と物性
- 28p-PSA-31 pr置換Y-Ba-Cu-O系の圧力効果
- S=1結合交替ハイゼンベルグ反強磁性鎖の磁性
- 28pPSB-36 スピネル型Cu_Zn_xIr_2S_4の圧力効果
- 30p-J-1 加圧による一次元反強磁性体のスピンギャップ誘導の試み