• The influence of(Ni, Co)Al_2O_4 spinel precipitates on the grain growth in(Ni, Co)O ceramics with 1.45 mol% Al_2O_3 Was investigated in the temperature range 1280 to 1380°C. Smaller precipitates preferentially dissolved and larger precipitates grew with increasing temperature and holding time, therefore, the growth mechanism of spinel precipiates was considered to be Ostwald ripening. The matrix grain size increased linearly as a function of particle size of spinel at 1280°C and 1360°C. Furthermore, the slope increased with increasing temperature, which indicates that the grain growth inhibition effect became weak. It is believed that higher solubility of Al_2O_3 into the matrix at higher temperature decreases the volume fraction of the spinel precipitates inhibited the grain growth of matrix.

• 社団法人日本セラミックス協会の論文
• 1996-01-01

著者

• 鈴木 了

  (株)日鉱マテリアルズ

• 鈴木 了

  (株)ジャパンエナジー総合研究所

• 瀬川 秀夫

  (株)ジャパンエナジー総合研究所

• 瀬川 秀夫

  (株)ジャパンエナジー精製技術センター

関連論文

• NiO-CoO及びNiO-CoO-MgO系セラミックスの緻密化及び機械特性
• SnO_2添加によるα-Fe_2O_3の還元抑制効果
• 昇温速度により組織制御した半導性(Ba, Sr)TiO_3の電気特性
• 湿式ボールミル粉砕したα-Fe_2O_3粉の焼結特性に及ぼすボールミルからの不純物の影響
• NiO-CoO固溶体の焼結挙動に及ぼす添加Al_2O_3粉末性状の影響
• NiO-CoO固溶体の焼結挙動に及ぼすAl_2O_3添加の影響
• Al_2O_3を添加したNiO-CoO固溶体の焼結体組織
• 擬ベーマイト粉末のキャラクタリゼーションと希硝酸中での解膠性
• レーザーCVD法による酸化物薄膜の低温合成
• レ-ザ-MOCVD法による酸化物薄膜の室温合成

スポンサーリンク