β'-o'複合サイアロンの遷移的液相焼結に及ぼす昇温速度の影響

スポンサーリンク

概要

• 論文の詳細を見る

• The transition liquid phase sintering is assumed to be a dominant densification mechanism of β' o' sialon. The liquid is formed by the reaction between silicon nitride, alumina and oxidized layer on the surface of silicon nitride particles. To study the effect of heating rate on densification of β' o' sialon, green compacts of a silicon nitride powder and boehmitesol were pre pared. The density of sintered β' o' sialons increased with increasing the heating rate. From the above result, it was considered that the transition liquid phase formed by the sintering with a high heating rate survives at a higher formation temperature than the case with a low heating rate.

• 社団法人日本セラミックス協会の論文
• 1995-12-01

著者

• 西尾 浩明

  Nkk総合材料技術研究所

• 薮田 和哉

  NKK総合材料技術研究所

関連論文

• 助剤無添加TiB_2の焼結性と力学的性質
• 717 窒化ケイ素成形体の Sinter/HIP 処理と焼結体の特性(セラミックス, 萌芽・境界技術, 日本鉄鋼協会第 113 回(春季)講演大会)
• β'-o'複合サイアロンの遷移的液相焼結に及ぼす昇温速度の影響
• β'-o'複合サイアロンの遷移的液相焼結に及ぼす酸素含有量の影響
• β'-o'複合サイアロンの組織,機械的性質に及ぼす焼結体作製プロセス時の酸化の影響
• 画像解析法によるβ'-o' 複合サイアロン焼結体中の相の定量
• 都市ごみ焼却灰溶融スラグを用いたロックウール
• TiB2-(2mol%Y2O3-ZrO2)焼結体の作製と機械的性質
• TiB2-ZrO2焼結体の作製と機械的性質

スポンサーリンク