• Different alumina characteristics of a raw material were tested in the glaze composition with a view toward overcoming difficulties in forming the intermediate layer during the fast firing process of porcelain tiles. The alumina samples, obtained by dehydrating aluminum trihydrate and grinding for various periods, had different particle size distributions. An outstanding improvement in the tile quality was observed for the fine grained alumina, which was expected to dissolve rapidly in the glaze melt. Differences in the internal tensions between glaze and body were also observed. The acquired characteristics and effects of the intermediate layer formed between body and glaze in relation to the alumina grain size are discussed.

• 社団法人日本セラミックス協会の論文
• 1995-04-01

著者

• 新開 誠司

  (株)INAX建材技術研究所

• 新開 誠司

  (株)inax第1生産技術研究所

• 新開 誠司

  (株)inax 窯業技術研究室

• 富崎 マルセロ

  (株)INAX第1生産技術研究所

関連論文

• 1163 外装タイルの都市型汚れに関する研究 : その4 表面親水化技術の応用
• 1534 外装タイルの都市型汚れに関する研究 : その3 外装タイルの表面処理の違いによる都市型汚れの評価
• 1533 外装タイルの都市型汚れに関する研究 : その2 TiO2光触媒による外装タイルの防汚効果
• 1532 外装タイルの都市型汚れに関する研究 : その1 都市型汚れの発生原因
• ラスタータイルの視感評価について
• アルミナの粒度が迅速焼成磁器タイル用釉薬に与える影響

スポンサーリンク