アルミナセラミックスの焼結及び微構造に及ぼすSiO_2とTiO_2添加の影響
スポンサーリンク
概要
- 論文の詳細を見る
Effect of SiO_2 and TiO_2 additions on the phase formation, sinterability, and microstructure of alumina ceramics was studied by differential thermal analysis, X-ray powder diffractometry, SEM, TEM, and dilatometry. Alumina-based mixture powders were prepared from starting materials of α-Al_2O_3 powder, Si(OC_2H_5)_4 and Ti(OC_3H_7)_4. The silica gel obtained from the hydrolysis of Si(OC_2H_5)_4 was coated on Al_2O_3 particles to form a thin surface layer. During the firing process, the silica gel didn't crystallize to cristobalite but reacted with Al_2O_3 to form mullite above 1500℃. The silica gel, mullite and/or Al_2O_3-SiO_2 liquid phase retarded the densification and the grain growth of alumina. As TiO_2 was added to the alumina-silica gel mixture, the sinterability was enhanced and the formation temperature of mullite was lowered.
- 社団法人日本セラミックス協会の論文
- 1993-06-01
著者
関連論文
- アルミナセラミックスの焼結に対するチタニア添加の影響
- TiO_2を添加したAl_2O_3-ZrO_2複合体の微細組織と機械的性質に及ぼす焼成雰囲気の影響(第2報) : TiO_2の添加量の影響
- TiO_2を添加したアルミナセラミックスの微構造と機械的性質に及ぼす生成物Al_2TiO_5の分解の影響
- 真空雰囲気で焼成したTiO_2を添加したAl_2O_3セラミックスの微構造と強度
- チタニアを添加したアルミナセラミックスの微構造と機械的性質(セラミックスの微細構造)
- 高純度アルミナ微粉末原料の粉末性状と焼結性
- 水熱合成したマンガン亜鉛フェライトの粉末特性と焼結性
- Al_2O_3-ZrO_2複合セラミックスの焼結と微細組織に及ぼすTiO_2添加の影響
- アルミナセラミックスの焼結及び微構造に及ぼすSiO_2とTiO_2添加の影響
- ムライトの焼結及び微構造に及ぼすY_2O_3添加の影響(第2報) : 液相の結晶化と粒子成長
- ムライトの焼結及び微構造に及ぼすY_2O_3添加の影響(第1報) : 相変化と焼結性
- ジルコニア強化アルミナ複合粉体の作製と焼結性
- 微細気孔分散アルミナセラミックスの作製
- TiO_2を添加したAl_2O_3-ZrO_2複合体の微細組織と機械的性質に及ぼす焼成雰囲気の影響(第1報) : Tiの拡散と焼結性
- 窒素雰囲気中で作製したCeO_2-Al_2O_3-SiO_2ガラスの性質