Effect of heat treatment conditions on properties of aqueous alumina green sheets was investigated. A suspension was prepared by mixing alumina, water and binder using a ball mill. The binder was acrylic ester and acrylic acid copolymer stabilized at pH 8.5 with a dilute ammonium solution. Green sheets were fabricated with a doctor blade. The suspension was cast on a PET film and dried at 70℃ 1h. The green sheets were heated at 80°, 100°, 120°, 150°, and 200℃ for 1h. The properties of green sheets, such as strength, extension, solubility in a dilute ammonium solution and adsorption behavior of moisture changed remarkably at the temperature of treatment from 120° to 150℃. FT-IR analysis revealed that changes in the properties of green sheets were caused by self-crosslinking of carboxylic groups of the binder. A small amount of water in a green sheet was found to be a kind of plasticizer.
- 社団法人日本セラミックス協会の論文
- 1992-12-01
著者
関連論文
- セラミックグリーンシートにおけるバインダーの役割 : 分散性とシート特性
- アルミナ水系懸濁液のレオロジカルな性質とグリーンシート特性
- テープ成形におけるサスペンジョンのレオロジー, 粘弾性挙動
- ドクターブレードによる分散
- バインダーの極性基数が懸濁液のレオロジカルな性質,グリーンシート特性に及ぼす影響
- グリーンシート特性に及ぼす熱処理温度の影響
- テープ成形における乾燥過程での懸濁液の粘弾性変化
- 懸濁液のレオロシカルな性質とアルミナグリーンシート特性 : 分散剤と結合剤の相溶性の影響
- セラミックグリーンシートの動的粘弾性と接着性