SiCにおける破壊靭性と耐酸化性に対する高融点金属ホウ化物粒子の分散効果

スポンサーリンク

概要

• 論文の詳細を見る

• Refractory metal borides (TiB_2, ZrB_2, HfB_2, VB_2, NbB_2, TaB_2, MoB and WB) were dispersed in SiC ceramics. The degree of densification by pressureless sintering for individual composites except MoB dispersion, appeared to be able to go beyond the 95% TD (theoretical density). The fracture toughness "K_<IC>" increased proportionally with increasing the amount of dispersed boride except MoB, from 3.2 MPa・m^<1/2> to about 5 MPa・m^<1/2> in 20 mol% dispersion. The oxidation behavior at 1500℃ in static air varied strongly, depending not only on the dispersed quantity but also on the kind of dispersed boride. For applications at 1500℃, preferable metal borides dispersed into SiC ceramics on manufacturing a tough and refractory composites were narrowed down to NbB_2 and WB.

• 社団法人日本セラミックス協会の論文
• 1992-08-01

著者

• 柘植 章彦

  (株)東芝研究開発センター

• 柘植 章彦

  (株)東芝 総合研究所

• 水谷 敏昭

  (株)東芝総合研究所

関連論文

• α-SiCの常圧焼結におけるホウ素系助剤の液状添加効果
• SiCウイスカ/Si_3N_4複合セラミックスの破壊挙動とその特性
• 3G06 AlN の焼結挙動
• 3B04 SiC ウィスカ/Si_3N_4 系複合セラミックスの破壊挙動とその特性
• 1B15 窒化アルミニウムの格子欠陥とカラーセンター
• 3A36 SiC ウィスカ/Si_3N_4 系複合セラミックスの特性
• 繊維強化セラミックスの開発動向
• 炭化けい素繊維複合高靭性窒化けい素セラミックス (ファインセラミックス)
• SiCにおける破壊靭性と耐酸化性に対する高融点金属ホウ化物粒子の分散効果
• ラトガース大学
• SiC-B-C系へのTaC等添加が非加圧焼結体の特性に及ぼす効果
• 繊維強化セラミックスの開発動向

もっと見る 閉じる

スポンサーリンク