金属炭酸塩とアルコキシドを用いたGlycine-Nitrate法によるBaTio_3粉末の合成と焼結

スポンサーリンク

概要

• 論文の詳細を見る

• BaTiO_3 powders were synthesized by glycime-nitrate process, using BaCO_3 and Ti[OCH(CH_3)_2]_4 as starting materials. Nitric acid was used as a solvent for the starting materials as well as an oxidant for self-combustion. The physical and chemical properties of as-prepared and calcined powders were characterized by helium pycnometer, X-ray diffraction, BET method and SEM. Single cubic phase of BaTiO_3 was obtained at 1000℃. When the glycine/cation molar ratio was 1.2, the reactivity of self-combustion was the highest and the degree of aggregates after calcination was very low. Relative density of 95% was obtained at 1400℃ when the molar of ratio 1.2 for glycine/cation was applied. The dielectric constant of the sintered body was about 2000 at 1400℃.

• 社団法人日本セラミックス協会の論文
• 1999-08-01

著者

• 文 志雄

  産業技術総合研究所シナジーマテリアル研究センター

• 李 弘林

  延世大学校セラミック工学科

• 金 龜大

  韓国科学技術研究院セラミック工程センター

• 朴 智愛

  延世大学校工科大学セラミック工学科

• 李 東牙

  韓国科学技術研究院セラミック工程センター

• 文 志雄

  延世大学校工科大学セラミック工学科

• 金 在東

  延世大学校工科大学セラミック工学科

関連論文

• NO_x分解用電極支持型電気化学セルの作製
• 一方向開気孔を有するセラミックス多孔体上に緻密な固体電解質薄膜の作製(セラミックスインテグレーション)
• 自動車排気ガス浄化用多層構造電気化学セルの設計(セラミックスインテグレーション)
• Ca-Co-O系層状構造酸化物配向セラミックスの異方的熱電特性
• Fe-Si系合金の熱電変換物性に及ぼす粉末酸化の影響
• 金属炭酸塩とアルコキシドを用いたGlycine-Nitrate法によるBaTio_3粉末の合成と焼結

スポンサーリンク