Silica fibers coated with alumina layers have been prepared using a solution of aluminum nitrate dissolved in 1, 3-butanediol. Texture and crystallite structures of the alumina have been examined from a viewpoint of thermal stability of the modified silica fiber. Amorphous alumina layer could be uniformly prepared on the silica fiber by impregnating the fibers in the aluminum solution. The alumina layer transformed to crude assemblies of alumina particles after aging the alumina-modified silica fiber in deionized water at 100°C. The alumina particles were composed of fibrils with 6nm in diameter and 100-150nm in length. The phase of the alumina also changed from amorphous to boehmite by aging and to γ-alumina by reheating at 500°C. The texture of the alumina on the silica fiber was thermally stable up to 1200°C for the aged samples. The surface area, based on the weight of the alumina, of the samples calcined at 1200°C for 5h and 30h were 84m^2・g^<-1> and 80m^2・g^<-1> respectively. XRD analysis showed no α-alumina formation the after above treatment, indicating that the crude texture of the alumina might suppress sintering because of small contact area among the alumina fibrils. Furthermore, it was found that alumina surface was covered with silica, and the silica might also restrain the surface diffusion of alumina not to induce the sintering. Both the crude texture of alumina and silica on alumina structure might effectively improve the thermal stability of the silica fiber.
- 社団法人日本セラミックス協会の論文
- 1999-02-01
著者
関連論文
- 超臨界水熱合成法による光触媒酸化チタンナノ微粒子の製造
- 産官学連携による高性能光触媒の研究開発とその実用化(高専の挑戦)
- チタンアルコキシジオレートの熱分解による角柱状TiO_2の調製とキャラクタリゼーション
- 角柱状酸化チタンの調製 : 形態に及ぼす溶媒の影響とその光触媒作用
- 最新光触媒 角柱状TiO2光触媒の開発とその応用 (特集 可視光型光触媒と光触媒技術の新展開)
- 木質バイオマスガス化触媒の調製
- アルミナによるシリカ繊維の表面修飾とその耐熱性
- ゾル-ゲル法によるアルミナ薄膜中の空孔径制御
- ゾル-ゲル法によるアルミナ薄膜の表面構造変化
- ゾル-ゲル法によるスポンジ状アルミナ薄膜の調製
- 高活性角柱状酸化チタン光触媒の開発とその応用 (特集 酸化チタン光触媒とその応用)
- アルミナ修飾シリカ繊維の調製とその水蒸気改質触媒への応用
- 超臨界二酸化炭素乾燥を用いた酸化チタンエアロゲル光触媒の合成