Si-Ti-C-O系繊維の1000℃における酸化挙動
スポンサーリンク
概要
- 論文の詳細を見る
The oxidation behavior of three kinds of Si-Ti-C-O fibers, TF1(18), TF2(12) and TF2(18), was investigated. TF2(12) with 12 mass% of oxygen content and TF2(18) with 18 mass% oxygen content synthesized from a polytitanocarbosilane (PTC2) with lower polyborodiphenylsiloxane content, had higher tensile strength after heat treatment at 1000℃ in air than TF1(18) with 18 mass% oxygen content synthesized from an another polytitanocarbosilane (PTC1). After heat treatment at 1000℃ for 500h, an oxide layer was formed on each fiber's surface. The oxide layer on TF1(18) was cristobalite, and a lot of cracks was observed on it, whereas that on TF2(12) and TF2(18) contained amorphous material. The free carbon content in TF1(18) was higher value than that of another two fibers.
- 社団法人日本セラミックス協会の論文
- 1997-05-01
著者
関連論文
- 透過型分析電子顕微鏡によるSi-Ti-C-O繊維 : ムライトマトリックス系複合材料の界面観察
- Si-Ti-C-O繊維/PIPセラミックス複合材の高温時における非線型応力一歪特性
- Si-Ti-C-O繊維/PIPセラミックス基耐熱複合材の非線型力学特性
- チラノ繊維強化炭化ケイ素複合材料
- Si-Ti-C-O系繊維の表面構造がセラミック複合材料の特性に及ぼす影響
- CO処理によって表面に炭素層を形成させたSi-Zr-C-O繊維を用いたCMCの特性
- Si-M(M=Ti, Zr)-C-O繊維の耐酸化性
- ゾルゲル法酸化物を添加した新規なプレセラミックポリマーを前駆体とする Si-M-C-(O) 繊維の開発
- CMC用強化材としてのSi-Ti-C-O系繊維の改良
- 3次元織物Si-Ti-C-O系セラミック複合材の高温気流中における耐熱性評価
- ガラスシール型PIPセラミックス基三次元織物複合材の高温大気中クリープ挙動に関する考察(第二報)
- ガラスシール型PIPセラミックス基三次元織物複合材の高温大気中クリープ挙動に関する考察
- ガラスシールにより耐酸化性を改善したPCセラミックス基三次元織物複合材の高温大気中クリープ挙動
- ガラスシールにより耐酸化性を改善したPCセラミックス基 三次元織物複合材の高温大気中での応力-歪み挙動
- Si-Ti-C-O系繊維集合体セラミックスの微細構造及び破壊挙動
- Si-Ti-C-O系繊維の1000℃における酸化挙動
- Si-Ti-C-O(チラノ)繊維中のβ-SiCナノ結晶クラスターの形成