鋼線の疲労に関する研究(第2報)(硬鋼線の軸方向残留応力に及ぼす減面率および低温焼鈍の影響、ならびに軸方向残留応力が存在していないと仮定した場合の回転曲げ疲労限度について)
スポンサーリンク
概要
- 論文の詳細を見る
This investigation was planned for researching the effect of the total reduction by drawing and the low temperature annealing upon the distribution of longitudinal residual stress of 0・65%C steel wire, drawn at various reductions from 60% to 90%, with subsequent annealing in the range 150℃ to 400℃. The diameter of all these wires was 1・3mm. For the measurement of the longitudinal residual stresses existing in these small wires, present writers adopted the dissolving method by acid, that is, the outer layers of the wire were successively dissolved off by 10% NHO_3 and at each time the change of the gauge length was measured by the micro-comparator. And then that distribution of longitudinal residual stress was calculated by Heyn's formula. The results obtained were as follows : All wires tested had the similar distribution of longitudinal residual stress, that is tension in outer part and compression in inner part and the maximum tensile stress existed near the surface. For both wires as-drawing up to 85%, and beyond this reduction it decreased. The release of residual stress by low temperature annealing was remarkable in case of over 300℃. From the fatigue limits of these wires reported in 1st report, the fatigue limits of these wires, on the assumption that these were no residual stresses, were calculated with the maximum tensile residual stresses measured in this investigation. As the result of this calculation, it was clarified that the maximum value of decreasing of the fatigue limit under rotating bending affected by the longitudinal tensile residual stress was found in the 85% reduced wire.
- 1960-01-15
著者
関連論文
- 鋼線の疲労に関する研究(第7報) : 硬鋼線の曲げ疲労における寸法効果
- 鋼線の疲労に関する研究(第6報) : 回転曲げと静ねじりの組合せ応力に対する硬鋼線の疲労強度について
- 鋼線の疲労に関する研究(第5報) : 硬鋼線の回転曲げ疲労強度に及ぼす軸方向残留応力の影響について
- 鋼線の疲労に関する研究(第2報)(硬鋼線の軸方向残留応力に及ぼす減面率および低温焼鈍の影響、ならびに軸方向残留応力が存在していないと仮定した場合の回転曲げ疲労限度について)
- 含銅鋼線の疲労強度について