オーステナイト系ステンレス鋼の腐食疲労に関する研究(第3報) : 予備繰返応力と予備腐食の影響
スポンサーリンク
概要
- 論文の詳細を見る
As repeated pre-stressing in air during the first stage, either overstressing at stress level 0.5 or 1 kg/mm^2 over the endurance limit with the cyclic repetition of 3.4×10^3 to 1.02×10^6, or understressing at stress level 1 kg/mm^2 below the endurance limit cycling from 1×10^6 to 7×10^7 was chosen, and followingly the specimen was exposed to air-saturated 5%H_2SO_4 at 25℃ to which the repeated stress equivalent to prior endurance limit was applied during the second stage, until it was led to failure. In order to give prior corrosion, rotating specimen under stress-free condition was exposed to air-saturated 5%H_2SO_4 at 25℃ for 1h to 100h as the first stage. After having drained out the acid after prior corrosion, the specimen was cleaned and dried, then was subjected to repeated stress in air as the second stage, and was led to failure. Secondary corrosion fatigue life in the second stage was slightly increased by primary overstressing in the first stage, but hardly any influence was given on secondary corrosion endurance by primary understressing in air. It was derived that, in view of these facts, endurance property conjoined with corrosion action was essentialy controlled by corrosion resisting property of metal within a given environment. Exposure to the aqueous acid solution as the first stage, gave no practical deterioration to the specimen in the following test in the second stage if repeated stress applied in this stage did not exceed prior endurance limit. However, if the repeated stress applied in this stage was beyond prior endurance limit, serious decrease of the fatigue strength at N cycles was exhibited by short time of prior corrosion, for some austenitic stainless steel, and the reverse was exhibited for some other austenitic stainless steel. It has been understood that this different tendency was presumably controlled by retained ductility of austenitic stainless steel, though corrosion resistance might be primary cause.
- 社団法人日本材料学会の論文
- 1962-10-15
著者
関連論文
- 腐食・防食の科学と工学(VI) : 防食工学 その3(防食管理)
- クロムイオンを含む沸騰濃硝酸中でのステンレス鋼の腐食
- 腐食研究体制の結集を
- 装置工業と腐食の管理 : 防食管理
- 水の性質と腐食
- オーステナイト系ステンレス鋼の腐食疲労に関する研究(第5報) : 表面圧延と焼ばめの影響
- オーステナイト系ステンレス鋼の腐食疲労に関する研究(第4報) : カソード電流の印加および酸化性カチオン添加の影響
- オーステナイト系ステンレス鋼の腐食疲労に関する研究(第3報) : 予備繰返応力と予備腐食の影響
- オーステナイト系ステンレス鋼の腐食疲労に関する研究(第2報) : 液温および繰返速度の影響
- オーステナイト系ステンレス鋼の腐食疲労に関する研究(第1報) : 希酸溶液中における316型ステンレス鋼の腐食疲労挙動