鉄鋼の高温ねじりによる加工性試験について
スポンサーリンク
概要
- 論文の詳細を見る
The hot torsion test has been adopted as an important means for the determination of a proper temperature for rotary piercing operation in the manufacture of seamless steel tube. However, according to the means heretofore applied in which the workability of steel is judged by the number of twists to failure, a comparison of ductility at high temperatures is qualitatively possible, but it is almost impossible to judge the occurrence of crack in working from that number of twists to failure. Secondary stress caused by torsion test being considered one of the important factors for occurrence of cracks in the making of steel tube, the author has tried to verify the fact by making experimental studies on seven kinds of carbon steel and five kinds of stainless steel so that the result may be applied to the determination of hot workability, and has confirmed the following matters : (1) Secondary stress which occur in torsion tests acts generally as tensile stress on the part of comparatively higher temperatures and as compressive stress on the part of lower temperatures. The temperature at the time of changing from tensile stress to compressive stress, that is, transition temperature varies with the kind of material. (2) The value of secondary tensile stress differs according to testing temperatures. There is a summit on the correlative curve of these two factors, and the shape of this part varies with the kind of steel and its components. In practice, a higher summit and a wider temperature limit can be acquired in case of more easily workable materials. (3) The temperatures where secondary tensile stress and the number of twists to failure respectively show the highest value do not necessarily coincide and defferent according to the kind of material. (4) Secondary tensile stress varies with strain rate when another testing condition is constant, and at the same time, in some kinds of steel, the highest value, which is not clear in the measurement by the number of twists to failure, is shown by this strain rate. They are, therefore, important factors for the study of strain rate and cracks occurred in the process of rolling. (5) Therefore, from the results mentioned in (1)〜(4), secondary tensile stress has a close relation with ductility of materials. The secondary tensile stress is possible applicable to the determination of cracks caused by working, which is difficult for us to judge by the number of twists to failure.
- 社団法人日本材料学会の論文
- 1961-03-15
著者
関連論文
- 155 鋼の圧縮加工限度について(加工, 製鋼加工, 日本鉄鋼協会 第 76 回(秋季)講演大会)
- 154 厚鋼板の曲げ加工性と熱間加工条件の関係(加工, 製鋼加工, 日本鉄鋼協会 第 76 回(秋季)講演大会)
- 140 低炭素厚鋼板の熱間成形性について(加工, 加工・性質, 日本鉄鋼協会第 71 回(春季)講演大会講演論文集 (II))
- 279 厚鋼板のスピニング加工性(熱間加工・加工性・ロール, 加工・性質, 日本鉄鋼協会 第 78 回(秋季)講演大会)
- 252 引張り・せん断試験による厚鋼板の曲げ加工性の評価(部会報告講演会・加工, 加工・性質・分析, 日本鉄鋼協会 第 82 回(秋季)講演大会)
- 2-23 鋼の耐力に対する測定法の検討
- 切欠き圧縮試験による鍛造性の評価
- 鉄鋼の研究における材料試験の役割
- 熱間ねじり試験による鉄鋼の熱間加工性の評価に関する研究
- 討-10 熱間捩り変形様式の分類と 2 次応力の挙動について(III. 熱間捩り試験による鋼の加工性の評価, 討論会講演論文 日本鉄鋼協会第 72 回講演大会講演論文集(II))
- 98 高温における鋼の捩り加工限度について(加工, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 鉄鋼の高温ねじりによる加工性試験について
- 61 鉄鋼の高温捩りによる加工性試験について(加工, 第 59 回(春季)講演大会講演大要)