ROLE OF GRAIN BRIDGING DEGRADATION OF SMALL CRACK ON CRACK PROPAGATION BEHAVIOR IN POLYCRYSTALLINE ALUMINA UNDER CYCLIC LOAD
スポンサーリンク
概要
- 論文の詳細を見る
In order to investigate the effects of grain bridging degradation on the cyclic fatigue in polycrystalline alumina, crack propagation tests were carried out under cyclic load and static load. Two kinds of small semi-elliptical surface crack were introduced by Knoop indenter. Polishing the surface layer, the residual stress around the Knoop indentation was completely removed. The cyclic loading accelerates crack propagation in small crack as the same as in long crack. On the other hand, measuring and analyzing the crack opening displacement(COD) of 350μm crack, we determined the net stress intensity factor K_<Itip>. Under the cyclic load, the reduction of bridging force resulted in an increase in K_<Itip> which, in turn, accelerated the crack propagation rate. Furthermore, it is found that bridging degradation mechanism under cyclic loading does occur, but that this mechanism is not sufficient to completely account for "fatigue crack growth in ceramics".
- 社団法人日本材料学会の論文
- 1998-03-15
著者
-
Kishimoto Hidehiro
Department Of Mechanical Systems Engineering Faculty Of Engineering Toyota Technological Institute
-
Kishimoto H
Department Of Mechnical Systems Engineering Toyota Technological Institue
-
Ueno Akira
Department of Internal Medicine, Division of Cardiology, Nippon Medical School
-
Ueno Akira
Department Of Mechnical Systems Engineering Toyota Technological Institue
関連論文
- PE-282 Management of Ventricular Tachyarrhythmia following PTSMA : Characteristics in Highly Risked HOCM Whom Indicated both PTSMA and ICD-implantation, is PTSMA harmful?(Cardiomyopathy, basic/clinical(04)(M),Poster Session(English),The 72nd Annual Scient
- A Prospective Study on the Risk-Stratification for Patients With Non-Sustained Ventricular Tachycardia Using a Novel Algorithm
- Influence of Water Vapor on Crack Propagation Behavior of Sintered Silicon Nitride under Cyclic Load : On the Substantial Cyclic Load Effect
- Cyclic Fatigue in Ceramics
- QUADRICUSPID AORTIC VALVE PERFORATION RESULTING FROM BACTERIAL ENDOCARDITIS : 2-D Echo- and Angiographic Diagnosis and its Surgical Treatment
- Study on Lymphokine Activated Killer(LAK) Cells I. Improved LAK cell induction in vitro
- A Case of Renal Cell Carcinoma with Lung Metastases Treated with Adoptive Immunotherapy
- In vitro Production of Tumor Necrosis Factor (TNFα/Cachectin) from Human Peripheral Blood Monocytes Stimulated with Bacillus Calmette-Guerin. - A Possible Mechanism of BCG Therapy
- Potentiating Effect of Buserelin Acetate,an LHRH Agonist,on the Proliferation of Ventral Prostatic Epithelial Cells in Testosterone-Treated Castrated Rats
- Tensile Fracture Behavior of UV Light Irradiated PBO Fiber
- Effects of ONO : 2235, an Aldose Reductase Inhibitor, on Muscarinic Receptors and Contractile Response of the Urinary Bladder in Rats with Streptozotocin : Induced Diabetes
- A Case of Disseminated Testicular Seminoma Successfuly Treated with Combination Chemotherapy and Cytoreductive Surgery
- Unusual Coarctation of the Aorta with a Large Saccular Aneurysm
- ROLE OF GRAIN BRIDGING DEGRADATION OF SMALL CRACK ON CRACK PROPAGATION BEHAVIOR IN POLYCRYSTALLINE ALUMINA UNDER CYCLIC LOAD
- Left Ventricular Morphometric Estimation of the Coarctation Complex in the First Year of Life
- ADRENOLYTIC PROPERTY OF NEM IN THE GUINEA PIG ATRIA IN VITRO
- FURTHER EVIDENCE FOR NEGATIVE INOTROPIC ACTION OF ACETYLCHOLINE
- Successfully Operated Obliterative Brachiocephalic Arteritis (Takayasu) Associated with the Elongated Coarctation
- HEMODYNAMIC EFFECTS OF ORALLY GIVEN CORONARY VASODILATORS
- Effects of SiO_2 Particles on Deformation of Mechanically Milled Water-Atomized SUS304L Powder Compacts
- THE USE OF THE ROLLING MANOMETER SYSTEM FOR MEASURING CORONARY BLOOD FLOW