ELECTRODEPOSITION AND SURFACE PROPERTIES OF NICKEL-PTFE COMPOSITE FILM

スポンサーリンク

概要

• 論文の詳細を見る

• Ni-PTFE composite films with water repellency have been prepared by the electrodeposition in the nickel sulfamate plating bath in which PTFE fine particles are suspended by using a cationic surfactant. The maximum content of PTFE in the composite film was 17 wt%. Above the contents of 12 wt%, the contact angle of a water drop on the surface reached 156゜ in maximum. The surfactant was co-deposited with PTFE particles in the electrodeposited Ni-PTFE composite film. This causes that the water repellency on the surface of the film falls after the neutral salt spray test(NSS)and the thermal cycle tests. The heat-treatments above 300℃ were effective to maintain the water repellent surface even after the weathering tests, while the surface morphology changed by the heat-treatment.

• 社団法人日本材料学会の論文
• 1998-09-15

著者

• Ibe T

  Industrial Technical Center Of Fukui Prefecture Fukui Jpn

• Ibe Toshio

  Industrial Technical Center Of Fukui Prefecture

• KIYOKAWA Hajime

  Kiyokawa Plating Industry Co., Ltd.

• CHONG Yong-Bo

  Reseach Institute for Applied Science

• YONEZAWA Susumu

  Department of Material Science and Engineering, Faculty of Engineering, Fukui University

• TAKASHIMA Masayuki

  Department of Material Science and Engineering, Faculty of Engineering, Fukui University

• Chong Y‐b

  Reseach Institute For Applied Science

• Takashima Masayuki

  Department Of Material Science And Engineering Faculty Of Engineering Fukui University

• Yonezawa Susumu

  Department Of Material Science And Engineering Faculty Of Engineering Fukui University

• Kiyokawa Hajime

  Kiyokawa Plating Industry Co. Ltd.

• Takashima Masayuki

  Department of Industrial Chemistry, Faculty of Engineering, Fukui University, 3-9-1, Bunkyo, Fukui 910

関連論文

• ELECTRODEPOSITION AND SURFACE PROPERTIES OF NICKEL-PTFE COMPOSITE FILM
• Mechanical Properties of Cr-Ni-N Films Deposited on Pre-Nitrided Steels
• Electrochemical Behavior of LiMn2O4 with Fluorine-Carbon Nanocomposite Surface (特集 ナノカーボン)
• Preparation of Lithium Hexafluorophosphate from LiF and P in Fluorine Atmosphere
• Valproic Acid-induced Hearing Loss and Tinnitus
• The Surface Modification of Graphite Particles by Direct Fluorination
• Preparation of Pure LiPF_6 Using Fluorine Gas at Room Temperature
• Orange Emission of TbF_3-Containing Fluoride Oxide Glass
• Formation of Refractory Carbide and Nitride Nanofibers by Thermal Decomposition of Poly(vinyl alcohol)-Titanium Lactate Hybrid Nanofibers
• Glaze-Slurry Particle-Size Distribution Influences on Physical Properties of Some Kutani-ware Glaze

スポンサーリンク