Formation Energy of Superlattice in Ni_3Fe (II) Kinetics of the Superlattice in the Stage of Local Ordering

スポンサーリンク

概要

• 論文の詳細を見る

• The change of the internal energy of Ni_3Fe superlattice during cooling processes was studied by specific heat measurement for various rates of cooling. After eliminating the part of the internal energy due to magnetic transformation, it was shown that the formation of local order starts already at 600℃ on cooling, and its rate attains a maximum at 520℃, decreasing to zero at about 400℃. The specific heat curves on cooling do not show any anomaly at 500℃, which is critical temperature for the long range order. The formation rate of local order at steady temperature annealing was also studied by keeping the specimen at 500℃ and observing the heat of evolution directly. It was confirmed that the rate of local order formation is large enough to be observed at this temperature. It decreases monotonously and becomes zero after about five hours annealing. These data are all consistent with our previous assumption that one of the two steps' precesses of the formation of superlattice in Ni_3Fe at 490℃ is the development of local order which has no critical temperature.

• 社団法人日本物理学会の論文
• 1954-06-25

著者

• Iida Shuichi

  Faculty Of Science University Of Tokyo

関連論文

• Origin of the Uniaxial Anisotropy in Iron-Cobalt Ferrites
• Formation Energy of Superlattice in Ni_3Fe Part(IV) : A Theoretical Treatment of Vacancy Migration and Disorder-order Transformation in Alloys
• Formation Energy of Superlattice in Ni_3Fe (II) Kinetics of the Superlattice in the Stage of Local Ordering

スポンサーリンク