The Magnetic and Thermal Properties pf the Intermetallic Compound MnHg
スポンサーリンク
概要
- 論文の詳細を見る
The magnetic susceptibility and the specific heat of powdered specimens of the intermetallic compounds with the compositions of MnHg and Mn_2Hg_5 were measured from the boiling point of liquid air up to 400°K. The thermomagnetic curve showed a break at about 200°K for MnHg. A peak was found in the specific heat vs. temperature curve at 198.5°K, which corresponded to the breaking point in the susceptibility. From the amount of this anomalous heat absorption, the anomaly might not be attributed to the transition from the antiferromagnetic to the paramagnetic state. The magnetization curve for MnHg at the liquid air temperature changed a slope at about 13KOe. An interpretation is given for the findings mentioned above.
- 社団法人日本物理学会の論文
- 1965-06-05
著者
-
OHASHI Masayoshi
The Research Institute for Iron, Steel and Other Metals, Tohoku University
-
Ohashi Masayoshi
The Reseaarch Institute For Iron Steel And Other Metals Tohoku University
関連論文
- Electric Conductivity and 3d-Electron Distribution in CuCr_2Se_Br_x : CHALCOGENIDE SPINELS : OPTICAL, ELECTRICAL AND MAGNETIC PROPERTIES
- Magnetic Properties of CrSb
- A High Pressure Apparatus for Neutron Diffraction
- Insulator-Metal Transition in Sm_Gd_xS Induced by Temperature and Pressure
- Metamagnetic Properties of the Intermetallic Compounds ErAu and HoAu
- Electric Resistivity and Thermal Expansion of DyAu_2
- Weak Ferromagnetism of NiS_2
- New Type Metamagnetism in Co(S_xSe_)_2 : Exchange-Compensated Paramagnetism
- Observation of the Antiferromagnetic Ordering in La_2CuO_4
- Electric Resistivity of the Antiferromagnetic Compounds RAg_2(R=Gd, Tb, Dy, Ho and Er)
- The Pressure Effect on the Neel Point of an Antiferromagnetic Compound CrSb
- High-Field Susceptibility of Ferromagnetic β_1-MnZn
- Temperature Dependence of the High Field Susceptibility of CoCr_2O_4
- On the Magnetic Behavior of the Intermetallic Compound CoGa
- The Magnetic and Thermal Properties pf the Intermetallic Compound MnHg
- The Magnetic and Thermal Properties of the Intermetallic Compound MnHg
- Neutron Diffraction Study of CaFe_2O_4