アルミ合金桁の終局強度に関する研究 : IV アルミ合金桁のせん断強度について(2)
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of this study is to evaluate the strength increment beyond shear buckling of the web of the large aluminum alloy beam and to put actively the results of this study to practical use. As a fundamental trial, one panel with two rigid vertical stiffeners, material of which was A5083, binary alloy of Al-Mg system with non-heat treatment, was loaded by the pure shear force. From that results, then, the web buckling strength, behavior of web after buckling and the ultimate strength in bending of the panel are discussed and it is tried to compare A5083 with SS41 and also to compare ultimate strength in shear with that in bending. In this paper, the theoretical analysis is firstly carried out to discuss the strength of panel in shear and then the results of the experimental study is shown. From these studies, the following can be mainly indicated: 1) In elastic range the increments of the experimental ultimate strength to the theoretical buckling strength are larger than in inelastic range and the characteristic difference of materials appear in the behavior of web after buckling. After buckling, in SS41 the strength increment beyond shear buckling is very small, but in A5083 it is considerably large. 2) There may be no great difference among the theoretical ultimate strength values and the ultimate strength of their panels may be about from 2.0 to 2.5 times as large as the theoretical ultimate strength in the case of elastic buckling and the former may be about from 1.3 to 1.5 times larger than the later in the case of inelastic buckling. 3) In shear the strength increments beyond the buckling of web due to the tensin field formation are about from 1.5 to 2.0 times as large as in bending.本研究の目的は大型アルミ合金桁のウェブの後座屈強度を調べ, それを積極的に利用することにある. そのための基礎的試みとして, 剛なる垂直補剛材を配置したアルミ合金A5083(AL-Mg系2元合金, 非熱処理)の1パネルをとらえ, これにせん断力のみ作用させ, 結果生ずる座屈強度, 座屈後の挙動, 並びにパネルの終局強度に検討を加え, 併せてSS41材及び曲げ終局強度との比較を試みたものである. 文中, 最初にせん断パネルの理論強度につき論じ, 次いで実験的研究成果を示した. その結果, 1)終局強度の座屈強度に対する増分は, 弾性座屈が非弾性座屈より大きく, また座屈後の挙動は, 材質の特徴を表わし, SS41材はA5083材に比べ座屈現象発生後パネルの耐荷力は殆んど残らないこと. 2)終局強度の各理論値に大きな差は認められず, パネルの終局強度は弾性座屈でそれの2.0〜2.5倍程度, 非弾性座屈でそれの1.3〜1.5倍程度であること. 3)ウェブ座屈後の耐荷力は張力場形成により, 曲げのみ作用する場合に比べ, ほぼ1.5〜2.0倍程度高いこと. 等を指摘した.
- 香川大学の論文
- 1977-03-30
著者
関連論文
- 曲げ部材強度に及ぼす捩りの影響について : I 半円形片持梁について(1)
- 曲げ部材強度に及ぼす捩じりの影響について : III 溝形片持梁について
- 曲げ部材強度に及ぼす捩りの影響について : II 半円形片持梁について(2)
- アルミ合金桁の終局強度に関する研究 : IV アルミ合金桁のせん断強度について(2)
- アルミ合金板の耐荷力に関する実験的研究
- アルミ合金柱の耐荷力に関する実験的研究
- アルミ合金桁の終局強度に関する研究 : III アルミ合金桁の曲げ強度について (2)
- アルミ合金桁の終局強度に関する研究 : II アルミ合金桁のせん断強度について (1)
- アルミ合金桁の終局強度に関する研究 : I アルミ合金桁の曲げ強度について (1)