合金化溶融亜鉛めっき鋼板の耐パウダリング性に及ぼすめっき皮膜構造の影響(溶融めっき)(<特集>表面処理)

概要

論文の詳細を見る
Effect of coating structure on powdering resistance of galvannealed steel sheet was investigated and the followings are clarified. 1) Higher galvannealing temperature deteriorates powdering resistance. But slower cooling from higher temperature (500∿550℃) improves powdering resistance. 2) In the case of lower galvannealing temperature (=440℃), the powdering resistance is rather good, although the cooling rate doesn't affect powdering resistance. 3) Exfoliation of galvannealed steel sheet after tensile test correlates with amount of powdering evaluated from draw bead test. 4) Г_1-phase (Fe_5Zn_<21>) is formed along the interface of coating galvannealed at lower temperature (≦500℃) or cooled slowly from high galvannealing temperature. 5) The decrease of Г_1 ratio [Г_1/(Г+Г_1)] deteriorates powdering resistance.
社団法人日本鉄鋼協会の論文
1991-07-01