ラインパイプ用鋼の応力腐食割れに及ぼす陰極防食条件の影響

概要

論文の詳細を見る
Stress corrosion cracking (SCC) of buried line pipe steel was studied from practical aspects of view including cathodic protection conditions. The results obtained are summarized as follows : 1) The most probable occurrence of SCC on buried steel pipelines was thought to be limited to the sites of cathodic disbonding accompanied by corrosion rusts. 2) Cathodic protection current of not less than 1 mA/cm^2 could cause cathodic disbonding of protective coating on a steel pipe, and could form a sufficient concentration of alkali to produce carbonate-bicarbonate SCC. 3) The more predominant environment to produce SCC on a buried line pipe steel was thought not a caustic alkali solution but a carbonate-bicarbonate solution because of a high partial pressure of CO_2 in the soil. 4) Those pipelines which were cathodically protected at the polarization potential between -1000 and -1350 mV vs. Cu-CuSO_4 and at the cathodic current density of less than 1mA/cm^2 were thought free from SCC.
社団法人日本鉄鋼協会の論文
1983-10-01