製鉄ガス-重油混焼ボイラーにおけるオーステナイトステンレス鋼管の高温腐食(高温の酸化と腐食)(<特集>耐熱鋼・耐熱合金)
スポンサーリンク
概要
- 論文の詳細を見る
Changes of appearances and metallurgical structures occurred by high temperature corrosion in austenitic stainless steel tubes during long time use for superheaters and reheaters of BFG, COG and oil mixed fired boilers were investigated. Corrosion of this type is occurred by molten deposit containing Na, V, Fe, S and SO_2 in combustion gas, and is accelerated after long time operation over 20000hours. In corroded tubes, sulfidization, carburization and Cr-depletion were always observed, and corrosion is progressed by the cycles of (sulfidization→carburization→Cr-depletion→oxidization). On the basis of these results, the model of corrosion mechanism is presumed that scale on the tubes is changed and desolved into molten deposit at early stage and Cr in carburized zone under sulfidized layer is rapidly consumed through molten Ni-Ni_3S_2-eutectic by SO_2, CO_2 from molten deposit at progressed stage, and discontinuous oxidization of these Cr-depleted zones follows.
- 1979-06-01
著者
関連論文
- 238 Fe-2 at% Ti 合金の水素吸収による焼入硬化, 時効軟化(鉄鋼の性質・加熱および熱処理, 加工・性質・分析, 日本鉄鋼協会 第 82 回(秋季)講演大会)
- 水素を吸収した Fe-1.5% Ti 合金単結晶の引張変形
- 320 18Cr-15W-Ni 耐熱合金冷牽シームレス管の製造とその特性 : 原子力製鉄熱交用超合金の開発 (3)(耐熱鋼・耐熱合金 (II), 性質・分析, 日本鉄鋼協会第 93 回(春季)講演大会)
- 200 NCF-1 合金の中間温度域における延性低下(耐熱合金・制御圧延, 性質, 日本鉄鋼協会第 91 回(春季)講演大会)
- 製鉄ガス-重油混焼ボイラーにおけるオーステナイトステンレス鋼管の高温腐食(高温の酸化と腐食)(耐熱鋼・耐熱合金)
- 413 自由表面に近づいた双晶先端付近の応力集中(靱性・破壊, 性質, 日本鉄鋼協会 第 86 回(秋季)講演大会)