溶鋼の空気酸化によつて生成したマクロ介在物の生成機構について
スポンサーリンク
概要
- 論文の詳細を見る
Macroscopic inclusions were intentionally produced by promoting air-oxidation of steel. Relation of macroscopic inclusions to cast structure and effect of the condition of solidification of steel on the occurrence tendency of macroscopic inclusions were studied. Consequently the following results were obtained. 1) Macroscopic inclusions produced by air-oxidation of steel were disposed preferentially inside interdendritic spaces, and the occurrence tendency of them was influenced by the condition of solidification of steel. Therefore, macroscopic inclusions produced by air-oxidation of steel were nothing but secondary deoxidation products of oxygen (oxide) dissolved by air-oxidation having been precipitated during solidification of steel. 2) The growth mechanism of macroscopic inclusions which are very large in comparison with microscopic inclusions is thought to be as follows ; When the segregation of oxygen which occurred in melt not by phase change of liquid steel to solid and the enrichment of oxygen to interdendritic spaces by phase change happened together overlapping, a great amount of oxygen capable of growing to macroscopic inclusions is enriched and precipitated in the form of macroscopic inclusion. In order to show that the foregoing presumption is probable interpretation for the growth mechanism of macroscopic inclusions, the phenomena in which oxygen or tin had already segregated in melt not by cell formation were shown. 3) It was shown that macroscopic inclusions produced by air-oxidation contained calcium. From the result, it is concluded that some calcium can dissolve in molten steel, and that exogenous oxide particles may be floated out by simple mechanism according to Stokes' law qualitatively, and that there are, accordingly, only rare macroscopic inclusions in melt, and that exogenous oxide particles develop seldom into macroscopic inclusions.
- 社団法人日本鉄鋼協会の論文
- 1967-01-01
著者
関連論文
- 119 ESR 鋼塊におよぼす電極-鋳型径比の影響(特殊精錬・物性, 製鋼, 日本鉄鋼協会 第 87 回(春季)講演大会)
- 421 新ジョミニー試験法の開発(耐熱鋼・耐熱合金・相変態・マルテンサイト, 性質, 日本鉄鋼協会 第 95 回(春季)講演大会)
- 97 ESR 鋼塊の凝固遷移層について(ESR, 製鋼, 日本鉄鋼協会 第 97 回(春季)講演大会)
- 38 鋼の連續冷却變態曲線に就て(日本鐵鋼協會第 45 回講演大會講演大要)
- 210 放電ダル : ダルロールについて第 2 報(圧延ロール・冷間圧延の制御と計測, 加工, 日本鉄鋼協会 第 95 回(春季)講演大会)
- 209 グリットダル : ダルロールについて第 1 報(圧延ロール・冷間圧延の制御と計測, 加工, 日本鉄鋼協会 第 95 回(春季)講演大会)
- 438 バックアップロールの転動疲労について(ステンレス鋼・ロール, 性質, 日本鉄鋼協会 第 98 回(秋季)講演大会)
- 534 大気溶解材と Ca-CaF_2 をスラグとした特殊 ESR 材の諸性質の比較(ロール材・電磁鋼板, 性質, 日本鉄鋼協会 第 98 回(秋季)講演大会)
- 全般に対する討論 : 介在物の組成と生成機構(鋼の脱酸と非金属介在物 : 凝固時の脱酸進行により鋼塊中に生成する大型介在物, 第 72 回講演大会討論会討論集録)
- 静止浴における Al の単独, および共同脱酸速度について : 脱酸速度の研究 VIII / 撹拌鋼浴および静止鋼浴における 1 次脱酸生成物の浮上分離機構について : 脱酸速度の研究 IX
- 溶鋼の空気酸化によつて生成したマクロ介在物の生成機構について
- 溶鋼の脱酸反応機構に関する一考察
- 98 溶鋼の空気酸化によつて生成したマクロ介在物の生成機構について(非金属介在物, 日本鉄鋼協会第 70 回(秋季)講演大会講演論文集 (I))
- 97 溶鋼の脱酸反応機構に関する一考察(非金属介在物, 日本鉄鋼協会第 70 回(秋季)講演大会講演論文集 (I))
- 溶鋼の脱酸反応機構に関する一考察
- 高炭素クロム鋼中の非金属介在物の挙動に関する研究
- 74 アルミナ系介在物の生成に関する 2, 3 の考察(非金属介在物, 日本鉄鋼協会第 67 回(春季)講演大会講演論文集 (I))
- 112 地疵と微視的介在物との関係について(製鋼基礎, 日本鉄鋼協会第 66 回(秋季)講演大会講演大要)
- 79 空気酸化による地疵の生成について(製鋼・基礎・その他, 日本鉄鋼協会第 65 回(春季)講演大会講演大要)