An experimental study was made on the equilibrium of liquid pure iron and the controlled atmosphere of N_2-A mixture or N_2 only in the range of nitrogen pressure up to 2.3 atm., in the temperature range of 1566℃ to 1740℃, and the following results were obtained : (1) The solubility of nitrogen in liquid pure iron does not obey the Sieverts' law, and the nitrogen-solubility deviates positively from this law. (2) The equilibrium constant and the free energy change in the reaction which nitrogen dissolves in liquid iron are represented by the following equations : log K_N=-815/T-0.819 ΔF°=3, 730+3.75T (3) The activity coefficient of nitrogen in liquid pure iron is represented by the following equation ; log f^N_N=1.97%N__- This equation is blieved to be independent of temperature over the range 1566℃ to 1740℃, at least in the range 0∿0.070% nitrogen.
- 社団法人日本鉄鋼協会の論文
- 1959-02-10
著者
関連論文
- 応力除去焼なましわれ防止方法の検討 : HT80 鋼の応力除去焼なましに関する研究(第 2 報)
- 応力除去焼なましによる材質変化 : HT80 鋼の応力除去焼なましに関する研究(第 1 報)
- 306 応力除去焼なまし割れにおよぼす強度の影響 : HT80鋼の応力除去焼なましに関する研究(第5報)
- 305 脆性破壊発生特性におよぼす溶接線直角方向の残留応力の影響 : HT80鋼の応力除去焼なましに関する研究(第4報)
- 139 応力除去焼なまし割れ防止方法の検討 : HT80鋼の応力除去焼なましに関する研究(第2報)
- 138 応力除去焼なましによる材質変化 : HT80鋼の応力除去焼なましに関する研究(第1報)
- 228 100Kg/mm^2磁級高張力鋼の溶接ボンド部の靱性
- 321 ラインパイプ用極低 C-Ti 系非調質高張力鋼とその溶接性(厚板・ラインパイプ・制御圧延, 性質, 日本鉄鋼協会 第 95 回(春季)講演大会)
- 302 80kg/mm^2 級高張力鋼板の靱性に関する研究(焼戻脆性・高張力鋼, 性質, 日本鉄鋼協会 第 87 回(春季)講演大会)
- 665 微量 Ti 添加による加速冷却型 50 キロ級鋼板の靭性改善(制御圧延・制御冷却(ラインパイプ)・直接圧延(厚板), 材料, 日本鉄鋼協会 第 105 回(春季)講演大会)