熔融鉄炭素合金の脱炭反応に関する研究(IV) : 水蒸気による脱炭反応について

スポンサーリンク

概要

• 論文の詳細を見る

• The rates of carbon removal of molten Fe-C alloys containing 0.5∿4%C with water vapour of H_2-H_2O, O_2-H_2O gas system were measured by flow method. The results obtained were as follows. In the system of H_2-H_2O gas mixture, the rates of carbon removal were proportional to the partial pressure of water vapour between 7 and 32mmHg. The dissolved oxygen in the melt during the reaction was independent of the pressure of water vapour and in some degree higher than the equilibrium value. From these results the reaction was considered to take place on the interface. The specific rate constant was somewhat smaller than that with oxygen gas of the same pressure. The increased amounts of the carbon removal with water vapour in the addition of water vapour to oxygen gas were influenced by oxygen gas pressure. The oxidation of carbon monoxide formed to carbon dioxide in the carbon reaction with oxygen gas was remarkable, but in the presence of water vapour this oxidation almost did not take place.

• 社団法人日本鉄鋼協会の論文
• 1957-11-01

著者

• 勝藤 昌伸

  北海道大学理学部無機化学教室

• 勝藤 昌伸

  北海道学芸大学

関連論文

• 熔融鐵炭素合金の脱炭反應に關する研究 (II) : 脱炭速度に及ぼす酸素壓の影響
• 23 製鋼反應の速度論的研究 (VII) : 脱炭反應の不均一性に關する一實驗(日本鐵鋼協會第 47 囘講演大會講演大要)
• 77 製鋼反應の速度論的研究 (VI) : 熔鐵中の炭素の活動係數に及ぼす硅素の作用(日本鐵鋼協會第 45 回講演大會講演大要)
• 熔鉄のガスによる脱硫反応に関する研究 (I) : 酸素による脱硫速度恒数の測定
• 29 溶鉄による SiO_2 の還元速度(製銑, 日本鉄鋼協会第 61 回講演大会講演大要)
• 熔鉄のガスによる脱硫反応に関する研究 (III) : 多元系熔鉄の硫黄の相互作用係数と脱硫速度恒数
• 熔融鉄炭素合金の脱炭反応に関する研究(IV) : 水蒸気による脱炭反応について
• 熔鉄のガスによる脱硫反応に関する研究 (II) : 水素による脱硫速度恒数の測定
• 酸素製鋼の基礎條件について
• 熔融鉄炭素合金の脱炭反應に関する研究 (III) : 脱炭速度恒数の濃度依存について
• 76 製鋼反應の速度論的研究 (V) : 酸素壓と脱炭反應の活性化熱との關係(日本鐵鋼協會第 45 回講演大會講演大要)

もっと見る 閉じる

スポンサーリンク