肌燒鋼の不完全燒入れによる脆化について
スポンサーリンク
概要
- 論文の詳細を見る
Sometimes, case-hardening steel is very brittle after quenching, nevertheless its hardness is relatively low. The authors' experiment on the plain C, Cr-Mo and Ni-Cr case-hardening steel indicates that this brittleness is recognized when the steel which contains a mixed structure of ferrite and pearlite is quenched from a little higher temperature than A_1 point, even in a rapid heating, and is lowered with increase of the quenching temperature up to A_3 point, but a martensitic or sorbitic steel is not brittle after quenching from just above A_1 point. From these results and microstructure observation of quenched specimens, it is concluded that this brittleness is caused by partial quenching which changes pearlite portion of the mixed structure into high-carbon martensite ; that this high carbon martensite prohibits the deformation of ferrites ; and that it is because of no high carbon martensite produced in the martensitic or sorbitic steel by quenching from all temperature ranges that such steel does not exhibit the brittleness.
- 社団法人日本鉄鋼協会の論文
- 1954-08-25
著者
関連論文
- 5 フリュオソリッドシンダーより銅沈澱剤としてスポンジー鉄粉の製造に関する研究(第 51 回講演大会講演大要)
- 討 17 工具鋼のイオン窒化(IV 鉄鋼の表面硬化処理に関する最近の動向, 第 101 回講演大会討論会講演概要)
- 鋼の表面硬化法としての窒化
- 37 不銹鋼の表面硬化に関する研究 (II) : 18-8 不銹鋼の窒化と耐蝕性に関する研究(第 52 回講演大会講演大要)
- 126 不銹鋼の表面硬化に関する研究 (I) : 13% Cr 不銹鋼の高周波焼入とその応用(第 51 回講演大会講演大要)
- 39 鑄鐵の高周波燒入に関する研究 (II) : Si の影響についての基礎実験(第 49 回講演大会講演大要)
- 肌燒鋼の不完全燒入れによる脆化について
- 109 可鍛鑄鐵の高周波焼入 (III)(日本鐵鋼協會第 47 囘講演大會講演大要)
- 108 鑄鐵の高周波焼入に關する研究 (I) : 最新鑄鐵の高周波焼入(日本鐵鋼協會第 47 囘講演大會講演大要)
- 球状黒鉛鑄鐵の車輛用制輪子への應用
- 105 球状黒鉛鑄鐵の車輛用制輪子への應用 (II)(日本鐵鋼協會第 45 回講演大會講演大要)
- 29 可鍛鑄鐵の高周波燒入 (II)(日本鐵鋼協會第 45 回講演大會講演大要)
- 97 可鍛鑄鐵の高周波燒入(日本鐵鋼協會第 44 回講演大會講演大要)
- 肌燒鋼の不完全燒入による脆化について
- 肌焼鋼の不完全焼入れによる脆化について
- 13) 合金の凝固の際に起る容積變化に就て(第一報)(日本鐵鋼協會第拾四囘講演大會)
- 工具鋼の窒化
- 鑄鐵の燒鈍に關する研究(I)
- 9) 鑄鐵の焼鈍に關する研究 (I)(日本鐵鋼協會第 24 囘講演大會講演大要)