製鋼工場に於ける品質管理の一例
スポンサーリンク
概要
- 論文の詳細を見る
Quality control has been recently adopted in various fields of industry and now the authors gave a glance at it in their steel-making plant. Steel-making operations are divided into four parts ; namely material preparation, meltng, refining and teeming, so some examples in each operation were shown. 1. Material preparation : Pig iron and scrap steel were classified and the ratio of pig iron to scrap steel used was determined according to the quality of steel to be produced, in order to make succeeding operations easier. 2. Melting operation : In the melting period, the most suitable carbon content at melt-down was aimed at to get the shortest heat time, which proved to be 0.55% C and 0.65% C for sheet and plate steel respctively in the 35t O.H.F. and 0.45% C (sheet steel only) in the 70t O.H.F. In the acceleration of combustion by using oxygen through furnace-end burners, most advantageous method or "6-5-4 method" is being adopted. According to this method, oxygen flows into the furnace in the rate of 6m^3/min., 5m^3/min. and 4m^3/min. for the three periods of one-hour from the start of charging, 2 hours, therefrom and the remaining time till melt-down after that, respectively. 3. Refining : To improve the weldability of the hull plate, a chart was prepared which showed the suitable weight of ferro-manganese to be thrown into ladle to make Mn/C in steel over 2.5. 4. Teeming : In pouring, standard operations were as follows : a) To decrease the brick and clay marks of ingots, silica mortar was used and newly lined ladle was avoided. b) A wooden plate was floated over the molten steel in each of six molds around the central pouring well in the bottom pouring, in order to reduce violent metal splashes, which might cause scabs of ingots.
- 社団法人日本鉄鋼協会の論文
- 1953-09-25
著者
関連論文
- 71 アルゴン及び酸素の吹込による熔鋼中の水素及び窒素の除去について (II)(第 51 回講演大会講演大要)
- 67 純酸素転炉における溶鋼温度連続測定(転炉, 日本鉄鋼協会第 68 回(秋季)講演大会講演論文集 (I))
- 48 純酸素転炉による合金鋼の製造(製鋼, 日本鉄鋼協会第 67 回(春季)講演大会講演論文集 (I))
- 42 純酸素転炉における重油の使用 : 純酸素転炉における燃料の使用 III(製鋼, 日本鉄鋼協会第 67 回(春季)講演大会講演論文集 (I))
- 純酸素転炉による高炭素鋼の製造(純酸素転炉による高炭素鋼の溶製について)
- 57 純酸素転炉における冷銑の使用(製鋼・転炉, 日本鉄鋼協会第 65 回(春季)講演大会講演大要)
- 54 タールドロマイト煉瓦の使用結果 : 純酸素転炉の内張りについて II(製鋼・転炉, 日本鉄鋼協会第 65 回(春季)講演大会講演大要)
- 87 コークス使用上の諸問題 : 純酸素転炉における燃料の使用 II(製鋼・転炉, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)
- 86 コークスの冷材溶解能力 : 純酸素転炉における燃料の使用 I(製鋼・転炉, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)
- 78 タールマグネシア煉瓦の使用結果 : 純酸素転炉の内張りについて I(製鋼・転炉, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 製鋼工場に於ける品質管理の一例
- 優良高級仕上鋼製造に關する研究(製鋼部會報告)