鋼材の割疵に關する調査研究
スポンサーリンク
概要
- 論文の詳細を見る
The author investigated cracks in billets of semi-killed steel and obtained following results as the causes : 1. Variation of the crack index between ladles were larger than that within them. 2. The crack index of 2nd ladles were larger than 1st ladles. 3. The crack index became maximum at 0.20∿0.21% C content, and it increased with the S content under the same conditions of rolling temperature. 4. Under normal operations of soaking pit, a prolonged soaking time increased the crack index of charges. 5. The rolling temperature index "h" had positive correlation with the crack index of normal charges. 6. On variation of the crack index within ladle, it was found that Al charged into molds had increased the crack index of ingots.
- 社団法人日本鉄鋼協会の論文
- 1953-10-25
著者
関連論文
- 81 室蘭製鉄所転炉工場の設備と操業(製鋼・転炉, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)
- 9 酸素による熔銑の脱珪処理について(製銑, 第 58 回講演大会講演大要)
- 62 上吹転炉の脱硫に対する一考察(転炉, 日本鉄鋼協会第 66 回(秋季)講演大会講演大要)
- 101 鋳型伝熱におよぼす操業条件の影響 : 連鋳鋳型の伝熱機構について I(連続鋳造, 製鋼, 日本鉄鋼協会 第 87 回(春季)講演大会)
- 79 ランス・ノズルに関する 2, 3 の理論的考察 : LD 転炉におけるランス・ノズルの検討 III(製鋼, 日本鉄鋼協会第 70 回(秋季)講演大会講演論文集 (I))
- 78 多孔ノズルと単孔ノズルの操業比較について : LD 転炉におけるランス・ノズルの検討 II(製鋼, 日本鉄鋼協会第 70 回(秋季)講演大会講演論文集 (I))
- 60 転炉におけるマンガンについて(転炉, 日本鉄鋼協会第 69 回(春季)講演大会講演論文集 (I))
- 54 単孔ノズルによる吹錬方法の変遷について : LD 転炉におけるランスノズルの検討 I(転炉, 日本鉄鋼協会第 69 回(春季)講演大会講演論文集 (I))
- 70 純酸素転炉における砂鉄の使用について(転炉, 日本鉄鋼協会第 68 回(秋季)講演大会講演論文集 (I))
- 62 室蘭転炉工場 1300t 混銑炉の操業および修理経過について(鋳物・連続鋳造・混銑炉, 日本鉄鋼協会第 68 回(秋季)講演大会講演論文集 (I))
- 19 リムド鋼に於ける製品硫黄含有率に關する一考察(日本鐵鋼協會第 47 囘講演大會講演大要)
- 鋼材の割疵に關する調査研究
- 90 鋼材の割疵に關する調査研究(日本鐵鋼協會第 45 回講演大會講演大要)