鑄鋼材の基本的性質に就て (I)
スポンサーリンク
概要
- 論文の詳細を見る
Steel used for the casting should have special properties compared with the structural steel. These properties are analysed by the following classification : 1. Gas hole, shrinkage cavity 2. Hot tear 3. Weldability 4. Mechanical property 5. Fluidity To satisfy these properties, at first, compositions of the steel are studied and we acquired following results : 1. To prevent the happening of gas holes, gasses in the steel must satisfy following conditions, O_2<0.01%, (Mn>0.65%, Si>0.35%) H_2<0.0004%, N_2<0.005%. Shrinkage cavities are lessened when degassing are sufficient. 2. To decrease the defect of the hot tear, the steel must have fowllowing compositions ; S<0.01%, Mn>0.7%, and Al used for deoxidizer is apt to increase the hot tear, so that Al content is preferable under 0.05%. 3. Weldability of the cast steel is not so much inflnenced by compositions, but following compositions are preferrable for welding operation, less than 0.3% of C, and S must be as small as possible. 4. Mechanical properties of the cast steel are not so much influenced by the compositions, too, except C should be determined by the strength demanded. 5. Also, fluidity of the cast steel is not so much influenced by the normal compositions, To obtain good fluidity, the molten steel should have sufficient temperature. By the above mentioned results, necessary compositions of the medium carbon cast steel are summarized as follows. C<0.3%, Si>0.35%, Mn=0.7∿0.9%, P<0.05%, S<0.05%, O_2<0.001%, H_2<0.0004%, N_2<0.05%.
- 社団法人日本鉄鋼協会の論文
- 1949-08-25
著者
関連論文
- 電氣爐鑄鐵の性質に就て (II)
- 鑄鐵中の水素分析に就て
- プロペラ材料について
- 舶用ディーゼルエンジンシリンダライナについて
- 鑄鐵中の酸素に關する一考察
- 鑄鋼材熔製法に關する考察(補遺)
- 鑄鋼材熔製法に關する一考察
- 鑄鋼材の基本的性質に就て II
- 鑄鋼材の基本的性質に就て (I)
- 熔鋼による鑄巣發生に關する一考察
- 鑄鋼の高温亀裂に關する研究(第 3 報)
- 鋼鑄物の巣に關する二三の實驗結果に就て
- 鑄鋼の高温龜裂に關する研究 (II)
- 鑄鋼の高温龜裂に關する研究(I)