The size change of oxide particles in oxide dispersion strengthened (ODS) ferritic steels was quantitatively evaluated by X-ray diffraction and TEM. Althougth yttria (Y_2O_3) particles are thermodynamically stable and do not have any solubility limit in 13%Cr steel, after 48h mechanical alloying (MA) by high energy ball mill, peaks of Y_2O_3 or any other peaks of precipitates were not observed. The size change of oxide particles was detected by small angle X-ray scattering. Oxide particles became smaller with MA time. Small addition of titanium was very effective on refining of solid solutioning of oxide particles. By heating of as-MA powders above 1273K, precipitation of new oxide particles which were identified with yttrium and titanium bi-oxide. Recovery and recrystallization properties of ODS ferritic steels were influenced by Y_2O_3 and titanium content. Extrusion at low temperature was effective to make the grain with low dislocation density and low aspect ratio.