電着塗装時の電流変化と表面処理鋼板の耐クレータリング性能との関連(自動車用鋼板)(<特集>表面処理)
スポンサーリンク
概要
- 論文の詳細を見る
The effect of the electric current density during the electrodeposition coating on the anti-cratering of surface-treated steels was studied. 1) The electric current density during the electrodeposition coating varied with the time in the slow-start method and many current density peaks were observed. The first peak current density was named as i_A, the final peak i_B. 2) The i_B/i_A varied discontinuously with the applied voltage and the voltage, at which the i_B/i_A increases discontinuously, was named the critical voltage. 3) It was found that the critical voltage was correlated with the tendency for the cratering of surface-treated steels and the steel having the high critical voltage showed the good anti-cratering properties.
- 1986-06-01
著者
関連論文
- 電着塗装における鋼板の耐クレータリング性能に及ぼすりん酸塩処理皮膜の影響
- 電着塗装時の電流変化と表面処理鋼板の耐クレータリング性能との関連(自動車用鋼板)(表面処理)
- 自動車用表面処理鋼板に形成されるりん酸塩処理皮膜の状態解析
- X線光電子分光法とイオンマイクロアナリシス法によるリン酸塩皮膜結晶の組成解析
- リン酸塩皮膜結晶の形成に及ぼす浴中Mn2+成分の影響
- 連続焼鈍材への添加金属元素と箱焼鈍法による析出したFe3Cとがリン酸亜鉛系化成処理性におよぼす影響
- 燐酸亜鉛系化成処理特性に及ぼす自動車用鋼板の表面キャラクタリゼ-ション効果
- XPSによる塗膜の表面解析 (色材と機器分析)
- 自動車用表面処理鋼板の化成処理皮膜
- Hopeite 結晶の固体および液体状態におけるレーザーラマンスペクトル
- Influence of zinc phosphate films on deposition process of galvanostatic electrodeposition.