高速度工具鋼の焼入加熱時間と機械的性質の関係
スポンサーリンク
概要
- 論文の詳細を見る
In the earlier paper dealing with the underhardening of high-speed steel of 6-5-4-2 type, the effects of the austenitizing temperature and the holding time at the temperature on the mechanical properties were reported. And then the time was constant, that is, 45 sec. The present work was undertaken to determine the effects of heating temperatures and times of wider ranges than those of the previous work, e. g. the austenitizing temperatures were 1160℃ and 1200℃ for press tools and 1240℃ for cutting tools, and the immersing times were 10∿3000 sec and tempering temperatures were 200∿625℃. The results obtained are as follows : (1) If underhardening is employed for press tools (1160℃ for quenching and 300℃ for tempering), the longer the immersing time the better the bend strength. (2) In case of cutting tools, a good abrasive resistant property is obtained when the steel is tempered at 550℃, and a high bend strength is associated with the hardness values of Hv 800∿850. (3) If better toughness rather than red hardness is required for tools, the tempering temperature should be as high as 600℃. By this tempering the range of bend strength over 400 kg is very wide. (4) When quenched hardness are about Hv 800, microstructure is consisted of residual carbides and the mixture of martensite and austenite. And this structure is obtained when immersing time is over 300 sec at 1160℃, 100 sec at 1200℃ and 30 sec at 1240℃. (5) The higher the temperature and the longer the time of immersing, the larger the austenite grains grow. And particularly, when austenitizing temperature is higher, the effects of immersing time on austenite grain-size are remarkable. (6) When the austenitizing temperature is low or immersing time is short, the grain-boundary disappears by the low tempering. But in case of the high temperature and long immersing time, the grain-boundary disappears by the tempering at about 500∿525℃.
- 社団法人日本鉄鋼協会の論文
- 1970-05-01
著者
関連論文
- アモルファス合金中の固溶水素の熱放出スペクトルとその理論的検討
- 合金工具鋼 (SKD11) の焼入加熱時間と機械的性質の関係
- 164 合金工具鋼 (SKD11) の焼入加熱時間と機械的性質の関係(工具鋼・その他, 加工・性質・分析・検査・計測, 日本鉄鋼協会第 84 回(秋季)講演大会)
- 高速度工具鋼の焼入加熱時間と機械的性質の関係
- 186 冷間加工されたパーライト鋼(ピアノ線)の焼なましについて(低合金鋼・鋼線, 性質, 日本鉄鋼協会 第 76 回(秋季)講演大会)
- 冷間鍛造用型としての高速度鋼の熱処理について
- 143 析出硬化鋼の時効硬度および組織におよぼす加工の影響 : 析出硬化型高速度鋼の研究 II(高張力鋼・合金鋼, 日本鉄鋼協会第 70 回(秋季)講演大会講演論文集 (II))
- 148 ショットピーニング後の焼鈍, ショットの投射速度などの影響 : ショットピーニングを行なつた弁ばねの硬度, 残留応力および疲労限について II(性質, 日本鉄鋼協会第 69 回春季講演大会講演論文集 (II))
- 147 ショットの形状, 直径およびピーニング時間の影響 : ショットピーニングを行なつた弁ばねの硬度, 残留応力および疲労限について I(性質, 日本鉄鋼協会第 69 回春季講演大会講演論文集 (II))
- 148 析出硬化型高速度鋼の組成と硬度の関係 : 析出硬化型高速度鋼の研究 I(性質, 日本鉄鋼協会第 65 回(春季)講演大会講演大要)
- 鋼の高温脆性
- 鋼の高温脆性
- 硼素鋼の熱膨脹履歴曲線に関する一考察
- 優れた水素放出特性をもつMg系ナノ構造合金の電顕組織観察
- マグネシウム系ナノ構造合金における水素の存在状態と放出機構
- 超急冷法で作製したナノ構造Mg基合金の水素吸蔵・放出特性とその機構
- 水素顕微鏡によるMg-Ni系2相合金表面に吸着・吸蔵した水素の2次元分布状態の観察
- 水素による固相反応の促進と抑制
- Hydrogen Enhancement of Interlayer Reaction in Ni/V Bilayer
- 面心立方金属中の水素と合金元素の相互作用
- アモルファス・ナノ構造合金の水素吸蔵 (材料と水素)
- アモルファス合金の水素吸蔵とその物性
- 冷間加工用工具鋼の焼入加熱時間