非磁性鋼の冷間加工硬化特性について : タービン発電機用非磁性鋼の研究 I
スポンサーリンク
概要
- 論文の詳細を見る
Influences of various factors such as solution treatment, cold work and stress relief on flow stress, cold work hardening characteristics and mechanical properties were tesed with the austenitic cold work hardening steels, 8Mn-8Ni-4Cr, 18Mn-4Cr, and 14Mn-6Ni-4Cr, which have been most widely utilized for non-magnetic retaining ring of turbo-generator. After tensile cold working up to 30% redaction of area at various temperatures from 20℃ to 500℃, tensile properties were studied at room temperature. The results obtained are as follws. 1) At the cold working temperature between 300℃ and 500℃ 8Mn-8Ni-4Cr showed the highest flow stress and 18Mn-4Cr the lowest, but at room temperature 18Mn-4Cr showed the highest flow stress on the contrary. 2) The investigation of the influence of cooling rate on the mechanical properties of the specimen with a 30mm squre bar cooled from solution temperature revealed that there was no difference between air cooling and water quenching with all of the specimens, except with the steel 18Mn-4Cr cold-worked at a relatively lower temperature, which showed better properties after water quenching. 3) As the result of changing the cold working temperature, tensile and proof strength were increased and elongation and reduction of area were decreased with increasing working temperature for 8Mn-8Ni-4Cr and 14Mn-6Ni-4Cr but for 18Mn-4Cr, tensile and proof strength were the highest when the specimen was cold worked at room temperature. Therefore cold work hardening was the most remarkable for 8Mn-8Ni-4Cr at the temperatures between 300℃ and 500℃ and for 18Mn-4Cr at the room temperature. 4) Influence of stress relieving temperature on the mechanical properties of these specimens after cold working at 400℃ and 500℃ was studied. There was no changes of the mechanical properties when stress relieved at the temperature below cold working temperature, but when stress relieved above cold working temperature, proof strength, elongation and reduction of area were all decreased and especially when relieving at 600℃ remarkable brittleness was caused because of carbide precipitation at grain boundary.
- 社団法人日本鉄鋼協会の論文
- 1964-01-01
著者
関連論文
- 138 応力除去焼なましによる材質変化 : HT80鋼の応力除去焼なましに関する研究(第1報)
- 123 構造用低合金鋼 (SNCM8) の焼入性能におよぼす合金元素の効果について : 構造用低合金鋼の研究 I(低合金鋼ほか, 第 58 回講演大会講演大要)
- 大型タービン軸実体の機械的性質について
- 高合金鋼の熱間加工性の改善に関する研究
- 3%Cr-Mo 鋼の諸性質におよぼす Ni, Cr および焼入冷却速度の影響
- 275 Cr-Mo 鋼の諸性質におよぼす Ni, Cr および焼入冷却速度の影響 : 大形ローター材の研究 I(試験検査・熱処理, 性質, 日本鉄鋼協会第 77 回(春季)講演大会講演)
- 274 11Cr-Mo-V 鋼の質量効果について : 11%Cr 系ローター材の研究 II(試験検査・熱処理, 性質, 日本鉄鋼協会第 77 回(春季)講演大会講演)
- 噴霧焼入法の研究
- 非磁性鋼の冷間加工硬化特性について : タービン発電機用非磁性鋼の研究 I
- 141 電動機軸材に関する研究(合金鋼その他, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 構造用低合金鋼 (SNCM8) の焼戻諸性質におよぼす合金元素の効果について : 構造用低合金鋼の研究 II
- 構造用低合金鋼 (SNCM 8) の焼入性におよぼす合金元素の効果について : 構造用低合金鋼の研究 I
- 153 冷間加工硬化型および析出硬化型非磁性鋼の硬化性について : タービン発電機用非磁性鋼の研究 III(性質, 日本鉄鋼協会第 66 回(秋季)講演大会講演大要)
- 78 含ボロンバネ鋼に關する研究(日本鐵鋼協會第 48 回講演大會講演大要)
- 136 タービン発電機用非磁性鋼の冷間加工による硬化について(性質, 日本鉄鋼協会第 60 回(秋季)講演大会講演大要)