高周波焼入における噴射液冷却の冷却能について
スポンサーリンク
概要
- 論文の詳細を見る
The hot junction of Pt-Pt・Rh couple was fixed at the centre of a 10mm ⨖ Ag ball. After heating up to 800℃ this ball was dropped into a spray of various quenching media and the cooling curves were plotted by oscillogram. From these data, the spray-quenching mechanism was considerd. As the result, the next conclusions were summarized. (1) The spray-quenching mechanism is similar to that of the conventional quenching essentially, but the cooling rate at the each stage of cooling curve becomes larger. In particular, vaper-film-breaking temperature rises extremely. (2) The quenching ability of oil emulsion was compared with that of water. (3) The effect of the flow rate on the cooling curve in spray quenching was made clear.
- 社団法人日本鉄鋼協会の論文
- 1962-11-01
著者
関連論文
- 各種太物工具鋼材の鍛造による方向性と熱処理による変形率について
- 18 各種太物工具鋼材の鍛造による方向性と熱処理による変形率について(第 53 回講演大会講演大要)
- 高周波焼入鋼の焼割れ感受性および焼入硬度におよぼす合金元素の影響について
- 高周波焼入鋼の焼割れ感受性におよぼす非金属介在物の影響について
- 164 高周波焼入の焼割れ感受性および焼入硬度におよぼす合金元素の影響について(熱処理, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 134 急速加熱した鋼の硬化層の疲れ強さと加熱冷却条件の関係(熱処理・肌焼鋼, 加工・性質・分析・計測, 日本鉄鋼協会第 80 回(秋季)講演大会講演)
- 161 保磁力を利用した表面硬化層深さの測定(計測・試験・分析, 加工・性質, 日本鉄鋼協会 第 83 回(春季)講演大会)
- 133 浸炭層の曲げ疲れ強さにおよぼす炭素量の影響(はだ焼鋼・強靱鋼, 性質, 日本鉄鋼協会第 79 回(春季)講演大会講演)
- 高周波焼入における噴射液冷却の冷却能について
- 高周波焼入鋼の残留応力におよぼす加熱条件および Ar" 変態の影響について
- 163 高周波焼入における噴射液冷却の冷却能について(熱処理, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 147 高周波焼入の焼割感受性に対する非金属介在物の影響について(性質, 日本鉄鋼協会第 60 回(秋季)講演大会講演大要)
- 117 高周波焼入鋼の残留応力に対する加熱条件, Ar" 変態の影響について(分析・性質, 第 59 回(春季)講演大会講演大要)