Mo 高速度鋼ならびに Co 高速度鋼中の炭化物について : 実用特殊鋼中の炭化物の電解分離による研究 IX

概要

論文の詳細を見る
The nature of carbides in Mo high speed steels (0-9-4-2, 6-5-4-2) and in Co high speed steel (18-4-1-20) were studied by electrolytic isolation method, with a view to clarify the role of Mo and Co in high speed steels. Carbides present in Mo high speed steels were M_6C, M_<23>C_6 and MC, likewise in the case of W high speed steels. The density of the carbides in Mo high speed steels was smaller than that of the carbides in W high speed steels, and so the percentage of carbides by weight in the former was smaller than that in the latter. By austenitizing trcatment, the carbides in Mo high speed steel were dissolved into matrix readily than the carbides in W high speed steel. Co high speed steel contained only a kind of carbide, M_6C. This carbide was usually hard to be dissolved into austenite. But the addition of Co in high speed steel had the effect of enlarging the solubility limits of W, Cr, V and other carbide forming elements in austenite, and served to promote the dissolving of M_6C during austenitizing.
社団法人日本鉄鋼協会の論文
1959-12-01