銅及酸素を含む鋼の高温脆性に就いて
スポンサーリンク
概要
- 論文の詳細を見る
As the cause of red-shortness, it is wellknown that copper metal freed from steel in oxidation penetrates into grain boundary and makes bending cracks on the surface of the steel at high temperatures. In our research of the low carbon steel containing copper content below 0.4% and ordinary commercial steel, we have found the fact that such low copper content is not serious factor, but heating in the strong oxidizing atomsphere is the main factor of the surface cracking ; i.e. the oxidation red shortness. Over 1200℃ the red shortness of the steel (on an Oelsen bending test machine) recovers and surface cracking diminishes. This suggests the existence of the temperature range of oxygen hot shortness and the authors ascertained the temperature range of the shortness both in hot bending test and hot impact test. Other factors such as sulphur are alsot conside red and heating in te atomsphere of hydrogen or mere prevention of strong oxidation surely makes less cracks. The surface cracks of the steel containing 0.1∿0.4% copper at the temperature range 900°∿1200℃ may be attributed to the oxygen inclusion of the steel.
- 社団法人日本鉄鋼協会の論文
- 1943-02-25
著者
関連論文
- 116 クリンガー・コッホ法による鋼中非金属介在物の定量方法の研究 (I) : 普通鋼の酸化介在物について(第 52 回講演大会講演大要)
- 鹽基性平爐鋼滓の化學的構成に就て
- 鹽基性電弧爐還元鋼滓の粘性に就て
- 銅及酸素を含む鋼の高温脆性に就いて
- 鋼塊の横目割傾向に就て
- 鹽基性平爐及び鹽基性弧光爐に於ける窒素の性状に就て