溶鋼の脱炭速度に及ぼす圧力,硫黄,酸素濃度の影響
スポンサーリンク
概要
- 論文の詳細を見る
The study was made on the rate of decarburization of molten steel in the low carbon co ntent range ([%C]≦0.1 mass%) under reduced prese ects of sulfur content of molten steel pressure and CO bubble formation in the metal bath. The chemical reaction rate constant at gas-metal interface was estimated. The value obtained was far greater than that of previously reported value by Harashima et al. using CO_2-CO-Ar gas. The reaction model analysis was made on the assumption that agitation by the formation of CO bubbles increased the interfacial area of bath surface. Three-step, i.e. mass transfer in metal and gas phases and chemical reaction at gas-metal interface were taken into consideration in the model.
- 社団法人日本鉄鋼協会の論文
著者
関連論文
- 減圧CAS-OBによる減圧下脱炭技術の開発
- 還元ガスによる溶鋼の脱窒速度
- 298 還元ガスによる溶鋼脱窒の実験室検討(精錬基礎, 製鋼, 日本鉄鋼協会第 111 回(春季)講演大会)
- Mg蒸気による溶銑の脱硫速度に及ぼす吹込条件の影響
- 半導体ガスセンサーを用いた溶鋼中水素迅速分析システムの開発(センサー)
- CaO-Al_2O_3系フラックスによる溶銑脱硫効率に及ぼすフラックス組成の影響(革新的高効率混合・分離リアクターの開発)
- 溶鋼の脱水素速度に及ぼす圧力,ガス吹き付けの影響
- 溶鋼の脱炭速度に及ぼす圧力,硫黄,酸素濃度の影響
- 溶鋼の脱水素速度に及ぼす圧力の影響
- 溶鋼の脱炭速度に及ぼす酸素, 硫黄濃度, 圧力の影響
- 溶鋼の吸窒素, 脱窒素速度に及ぼす圧力, 酸素, 硫黄, 窒素濃度の影響
- Na_2O-CaO 系フラックスによる溶銑の脱硫速度
- 溶銑脱りん速度に及ぼす攪拌力, 酸素供給速度の影響
- タンディッシュ内酸化雰囲気中でのArガス吹き付けによる溶鋼酸化速度
- Ca処理溶鋼における連続鋳造用ノズルへの介在物付着機構
- 溶鋼再酸化時の連続鋳造用ノズルへのアルミナ付着機構
- 溶鋼再酸化時の連続鋳造用ノズルへのアルミナ付着挙動
- 溶鋼再酸化時の連続鋳造用ノズルへのアルミナ付着挙動
- [分かり易い耐火物の反応」 耐火物-ガス間反応の速度論
- タンディッシュ注入溶鋼の酸化速度(タンディッシュ内溶鋼の酸化挙動-4)
- アルミナグラファイト浸漬ノズルの酸化速度
- タンディッシュ内溶鋼の酸化速度に及ぼす攪拌の影響の基礎的検討
- ブローホール欠陥発生に及ぼす耐火物・溶鋼間反応の影響
- ガス吹き込み型浸漬ノズルの割れ発生防止
- アルミナグラファイト浸漬ノズルと低炭素鋼の反応速度