ジェチレントリアミン五酢酸を用いて作製したBi系酸化物超電導体

スポンサーリンク

概要

• 論文の詳細を見る

• The superconducting Bi-Pb-Sr-Ca-Cu-O (BPSCCO) compound prepared from mixed mental-diethylenetriaminepentaacetate (DTPA) complexes has been investigated using SEM/EDAX, TG-DTA, XRD and four probe dc resistance. For precursors made from Mdtpa or triethylentetraminehexaacetate (TTHA) complexes, almost concordant metal distribution was obtained at different electron radiation areas (lmm2, 1μm2, 400nm2). Through the thermal decomposition of precursor, first production was 2001 phase at 400℃, then disappearance of 20O1 phase and formations of 22O1 phase and Ca2PbO4 occured in the temperature range of 500 to 700℃, finally 2212 phase was formed at 800℃ after disappearance of 2201 phase and Ca2PbO4. The critical current density Jc of BiPb0.2SrCal.2Cu1.7Ox with intermediate cold press was 4200A/cm2 at 77K and zerro field.　　Key words: superconductors, critical current density, bismuth, chelate, evaluation.

• 山形大学の論文
• 1993-01-30

著者

• 藤沢 忠

  山形大学工学部

関連論文

• ペンタクロロフェノールおよびその誘導に関する研究(第1報)ペンタクロロフェノールの精製および定量法
• カルシウムシアナミドよりシアン化物の合成
• 塩化シアンの合成
• ジェチレントリアミン五酢酸を用いて作製したBi系酸化物超電導体
• 可変波長レーザー誘起相関光音響分光法のオンラインデータ処理システム

スポンサーリンク