高水圧下における N- イプロピルアクリルアミド (NIPA) ゲルの相図
スポンサーリンク
概要
- 論文の詳細を見る
Pressure-induced volume phase transition of neutral and ionized N-isopropylacrylamide (NIPA) gels were examined for various temperatures. The volume ratio of the gels were measured from atomospheric pressure to 250MPa. The phase diagrams which are described by volume, pressure and temperature were obtained. It was found that the neutral gels underwent the continuous phase transition and the ionized gels did the discontinuous transition when the pressure was increased. In the higher pressure region, the swollen ionized gels gradually shrunk with increase of the pressure and underwent the shrunken state above ∿200MPa again. The results were discussed by using the theory describing the equilibrium condition of a gel.
- 1997-02-28
著者
関連論文
- 高分子ゲルを用いたリユーザブル吸水シート
- KCl結晶のImperfectionからの光散乱
- 30p-U-8 KCl:Pb^ からの光散乱
- ピリジン-水, 混合溶媒中における N-イソプロピルアクリルアミドゲルの体積相転移
- 偏光解消レイリー散乱による溶媒分子の配向緩和とN-イソプロピルアクリルアミドゲルの体積相転移
- 高水圧下における N- イプロピルアクリルアミド (NIPA) ゲルの相図
- 水圧によって誘起されたN-イソプロピルアクリルアミドゲルのスピノーダル分解
- 16a-B-13 C_6H_6液体の磁界点におけるRayleigh散乱
- NIPA ゲルの応用
- 偏光解消レイリー散乱による pNIPA ゲル中の溶質(ピリジン)の配向緩和と体積相転移
- 蛍光プローブによるゲル相転移の可視化
- アンチストークス蛍光映像法による水溶性ゲルへのプローブ溶質分子の吸着・拡散挙動の可視化
- 水圧による高分子ゲルの相転移
- 2a-B-2 溶媒圧急変化によるNIPAゲルの相分離
- 高圧溶媒中における高分子ゲルの相転移
- 29p-WA-5 溶媒圧による高分子ゲル中の濃度ゆらぎの発散
- 30p-ZF-5 NIPAゲルの体積相転移の圧力効果と圧縮率
- 27p-C-12 ゲルのガラス転移
- 4a-KG-4 SbI_3結晶の構造と光散乱
- 14a-S-6 層状物質BiI_3,SbI_3のBrillouin散乱
- 27p-K-4 BiI_3のBrillowin散乱
- 2a-NE-10 ピレン結晶の相転移
- 3a-NGH-13 PMMAのブリリュアン散乱とけい光
- Poly(N-isopropylacrylamide)ゲル内のRhodamine 101のアンチストークス蛍光(商船・理工学)
- 光散乱による水滴粒度分布測定に関する研究
- フラウンホーファー回折理論による液滴粒径測定法
- 汗濡れ損防止用再利用可能高分子ゲル吸水シート
- ポリスチレン-シクロヘキサンゲルの光散乱とスピノ-ダル線 (高分子ゲル-1-)
- 30a-P-3 目のレンズからの Brillouin 散乱
- 低温での高分子固体PMMAのBrillouin散乱
- 5p-AD-12 低温でのPMMAのBrillouin散乱
- 5p-U-3 アルカリハライドのBrillouin散乱強度の温度変化
- 6p-KH-9 Brillouin散乱によるイオン結晶の光歪定数の温度変化
- 高分子ゲルを用いたリユーザブル吸水シート