環境脆性破壊の発生
スポンサーリンク
概要
- 論文の詳細を見る
The process of formation of brittle cracks in embrittled materials by the effects of corrosive environment were studied by X-ray diffraction and transmission electron microscopic observations. In the case of stress corrosion tests of austenitic stainless steel, in spite of the small amount of plastic deformation, dislocation density increased under constant low tensile stress and after the half of the life times, many cracks were initiated. The initial states of these cracks are alike to G. P. zone in precipitation reaction. These cracks were also formed in the hydrogen charged steels. It could be considered that the initiation of cracks in the material which is fractured following no large ductile deformation may be done as the process.
- 山口大学の論文
著者
関連論文
- オーステナイト系ステンレス鋼における水素化物のX線的研究
- オーステナイト系ステンレス鋼の深絞り加工材の残留応力
- (1-20) 疲労亀裂の発生
- 光弾塑性法ならびにX線法による弾性・塑性集中応力の解析
- 大形構造物用X線応力測定装置
- 2-21 大型構造物用 X 線応力測定装置
- 回折線が拡散した場合の残留応力測定法について
- 日本におけるX線応力測定の現状
- 切欠き集中応力のX線的研究
- 水素吸蔵によるステンレス単結晶のひずみ分析
- 巨大構造物のX線応力測定について
- 大型鋳鋼品のX線による残留応力測定
- 材料強度研究に用いられるX線機器
- はん点状回折環を生ずる場合のX線応力測定
- (2-32) 斑点状回折環とそれによる応力測定
- (3-13) 鉄単結晶の水素誘起変形の研究
- 日本における微小焦点X線発生装置ならびに細束X線カメラの現状
- 日本におけるX線応力測定装置の現状
- 高張力鋼の水素ぜい性を硫化物応力腐食割れの関係についてのX線的研究
- 軟鋼の水素吸蔵に関するX線的研究
- 環境脆性破壊の発生
- オーテナイト系不銹鋼に於ける応力腐蝕割れに及ぼす水素の影響について
- 水素吸臓によって鉄鋼に誘起される諸現象
- オーステナイト系不銹鋼の応力腐蝕に関するX線的研究
- 材料学会X線材料強度部門委員会第2分科会取纏め 疲労のX線的研究(II)
- 材料学会X線材料強度部門委員会第2号分科会取纏め 疲労のX線的研究
- オーステナイト系不銹網の水素吸蔵に関するX線的研究
- オーステナイト系不銹鋼の環境脆化過程の観察
- オーステナイト系不銹鋼の水素吸蔵に関するX線的研究
- オーステナイト系不銹鋼の疲れ過程のX線的研究
- 粉末焼結体の性質に関するX線的研究
- 細束X線カメラについて
- 鉄鋼材料の塑性変形機構のX線的研究
- オーステナイト系不銹鋼の水素吸蔵についてのX線的研究
- 軟鋼の水素吸蔵に関するX線的研究
- 粉末焼結材の性質に関するX線的研究