<研究報告>ニトリルゴムの圧縮歪(第2報)
スポンサーリンク
概要
- 論文の詳細を見る
In the previous report (I), we have calculated instant-rigidity G_0, late-rigidity G_1, late shear viscosity η_1, and permanent shear viscosity η_2 which changed along to amount of sulfur, carbon, filler, etc, to that of rubber. As the result of calculation, we could reserch about the combination of rubber and other submaterials whose instant deformation was large and creep deformation was small. It was most desired condition that zinc oxide, carbon, stearic acid, sulfur were about 5, 40, 1.5, 3 Parts respectively to 100 parts of rubber. In this report, we have investigated that the amounts of accelerators of vulcanization and sulfur have influenced to compressed deformation, and late-deformation, and calculated G_0 G_1, η_2, respectively.
- 愛知工業大学の論文
- 1967-12-30
著者
関連論文
- 加圧下におけるオリゴメタクリル酸メチルの合成
- メタクリル酸メチルと四塩化炭素のテロメリゼーション
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第24報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第23報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第22報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第21報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第20報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第19報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第18報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第17報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第16報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第15報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第14報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第13報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第12報)
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第11報)
- P軌道元素中の電子の動きと元素の電気陰性度に就いて(第7報) : 3P軌道元素
- P軌道元素中の電子の動きと元素の電気陰性度に就いて(第6報) : 2P軌道元素
- P軌道原子中のπ電子密度とその分子の反応性に就いて(第10報) : 三原子及び四原子分子
- P軌道原子(原子は元素の構成単位)中のπ電子密度とその分子の反応性に就いて(第9報) : 二原子及び三原子分子(但しHを除く)
- P軌道元素中の電子の動きと元素の電気陰性度に就いて(第8報) : 4P, 5P, 6P軌道元素
- スチレンのテロメリ化反応
- 一酸化炭素変成触媒に関する研究(第1報)
- 学生の成績変動に就いての調査
- メタクリル酸メチルと四塩化炭素のテロメリゼーションにおける溶媒の添加効果
- 熱硬化性樹脂および合成ゴムの接着性 : 第1報. フェノール樹脂, エポキシ樹脂および合成ゴム
- ニトリルゴムの圧縮歪(第2報)
- ニトリルゴムの圧縮歪(第1報)