SURFACE FATIGUE CRACK GROWTH BEHAVIOR OF SWRH42A STEEL WIRE IN 3.5% NaCl SOLUTION UNDER CATHODIC OVER PROTECTION
スポンサーリンク
概要
- 論文の詳細を見る
- 2012-05-01
著者
-
Asakawa Kei-ichi
Faculty Of Marine Engineering Tokyo University Of Marine Science And Technology
-
Tabata Hiroshi
Faculty Of Marine Engineering Tokyo University Of Marine Science And Technology
-
MOTODA Shin-ichi
Faculty of Marine Engineering, Tokyo University of Marine Science and Technology
-
SUZUKI Yohnosuke
Tokyo University of Marine Science and Technology
-
Motoda Shin-ichi
Faculty Of Marine Engineering Tokyo University Of Marine Science And Technology