Sulfide Capacity of the CaO-SiO_2-MnO Slag at 1873K
スポンサーリンク
概要
- 論文の詳細を見る
The sulfide capacity of the CaO–SiO2–MnO slag through the entire composition range was measured at 1873 K using a gas–slag equilibration method and the effect of basicity and the activity coefficient of sulfide on the sulfide capacity of molten slag was investigated. Furthermore, the relationship between the sulfide capacity and the optical basicity of MnO–containing slags was evaluated in view of industrial applications. Sulfide capacity of the slag linearly increased by increasing the content of MnO not only at a given silica content but also at a fixed Vee ratio (=CaO/SiO2). The capacity and the modified Vee ratio (=(CaO+MnO)/SiO2) showed a good linear relationship. Assuming that the basicity and the stability of sulfide ion in the slag are proportional to the activity of MnO (aMnO) and the activity coefficient of MnS (γMnS), respectively, the composition dependency of sulfide capacity was well described by the changes in the ratio of aMnO to γMnS. The iso–sulfide capacity of the CaO–SiO2–MnO slag at 1873 K was constructed in the present study. The capacity contours seemed to rotate clock–wisely from the CaO–SiO2 binary side to the MnO–corner. The sulfide capacity increased with increasing ratio of MnO to CaO at relatively acidic region in which silica content greater than about 40 mass%, while the substitution of CaO by MnO does not significantly affect the capacity in the low silica region. The sulfide capacity generally increased with increasing content of MnO regardless of changes in the content of other constituents in multicomponent MnO–containing slags. It is necessary to take different values for the theoretical optical basicity of MnO in order to estimate the sulfide capacity of MnO–containing slags depending on the content of silica.
- 2011-08-15
著者
-
Park Joo
School Of Materials Science And Engineering University Of Ulsan
-
Kang Youn-bae
Graduate Inst. Of Ferrous Technol. (gift) Pohang Univ. Of Sci. And Technol. (postech)
-
Park Geun-ho
School Of Materials Science And Engineering University Of Ulsan
-
Park Joo
School Of Materials Sci. And Engineering Univ. Of Ulsan
-
Kang Youn-bae
Graduate Institute Of Ferrous Technology Postech
関連論文
- Phosphate Capacity of CaO-SiO_2-MnO-FeO Slag Saturated with MgO
- Hot Metal Desulfurization by CaO-SiO_2-CaF_2-Na_2O Slag Saturated with MgO
- Thermodynamics of Copper Dissolution into MnO-SiO_2-MnS Inclusion System
- Thermodynamic Analysis of Mn-depleted Zone Near Ti Oxide Inclusions for Intragranular Nucleation of Ferrite in Steel
- Thermodynamics of Titanium Oxide in CaO-SiO_2-Al_2O_3-MgO_-CaF_2 Slag Equilibrated with Fe-11mass%Cr Melt
- Discussion on "The Estimation of the Iso-viscosity Lines in Molten CaF_2-CaO-SiO_2 System"
- Electrochemical Method for Controlling the Interfacial Oxygen in Molten Fe with ZrO_2 Based Solid Electrolyte
- The Role of Iron Oxide Bearing Molten Slag in Iron Melting Process for the Direct Contact Carburization
- Control of MgO・Al_2O_3 Spinel Inclusions in Stainless Steels
- Carbide Capacity of CaO-SiO_2-MnO Slag for the Production of Manganese Alloys
- Sulfide Capacity of the CaO-SiO_2-MnO Slag at 1873K
- Numerical Analysis of Surface Tension Gradient Effect on the Behavior of Gas Bubbles at the Solid/Liquid Interface of Steel
- Structure–Property Correlations of CaO–SiO2–MnO Slag Derived from Raman Spectroscopy
- Sulfide Capacity of CaO–SiO2–MnO–Al2O3–MgO Slags at 1873 K
- Density Measurements of CaO–MnO–SiO2 Slags
- Thermodynamics of the MnO–FeO–MnS–FeS–SiO2 System at SiO2 Saturation under Reducing Condition: Immiscibility in the Liquid Phase
- Sulfide Capacity and Excess Free Energy of CaO–SiO2–MnO Slag Derived from Structural Analysis of Raman Spectra
- Numerical Analysis of Surface Tension Gradient Effect on the Behavior of Gas Bubbles at the Solid/Liquid Interface of Steel
- Structure-Property Correlations of CaO-SiO_2-MnO Slag Derived from Raman Spectroscopy