一方向強化CFRP材における繊維方向のヤング率の評価
スポンサーリンク
概要
- 論文の詳細を見る
The elastic modulus of unidirectional carbon fiber reinforced plastics (CFRP) was investigated by mechanical tests and analysis using finite element method (FEM). The mechanical tests are three points bending tests and tension tests. The analysis was examined by micro model and macro model. On the micro model, the 3-dimensional finite element method program created in consideration of the anisotropy of carbon fiber and the isotropy of matrix was applied to the hexagonal array model. On the macro model, the 2-dimensional finite element method program created in consideration of the anisotropy of CFRP was applied to the plane stress model using the triangle element. Consequently, it was found that the calculated data of the micro and macro model was larger than the experimental data. It was considered that the carbon fiber in the matrix was wound. Furthermore, the calculated data of the macro model in consideration of the angle θ of the direction of the carbon fiber was found to be in a reasonable agreement with the experimental data of the tension tests in case of θ = 0 ˜18° decided by the random number. The maximum of θ is considered to be small because that the Youngs modulus of the interface layer is smaller than that of the matrix.
- 一般社団法人 日本レオロジー学会の論文
- 2002-09-15
著者
関連論文
- アクリルフォーム接合テープを挟んだ金属板の制振性評価
- 動的粘弾性測定による硬質ポリウレタンフォームの動的弾性率,損失正接
- アクリルフォーム接合テープを貼り付けた熱硬化性ポリウレタンエラストマーのせん断損失正接
- 動的粘弾性測定による振動減衰能の測定--アクリルフォーム接合テープを挟んだシリコーンフォームの圧縮損失正接
- アクリルフォーム接合テープを挟んだマイクロセルポリウレタンフォームの圧縮損失正接
- アクリルフォーム接合テープを挟んだゴムの振動減衰能の測定
- 一方向強化および平織強化CFRP材における損失正接の周波数--温度依存性
- ビーズ法ポリスチレンフォームにおける動的圧縮弾性率の時間変化と温度特性
- 硬質ポリウレタンフォームにおける動的弾性率
- ポリ塩化ビニルフォームにおける動的粘弾性パラメータの時間変化、温度特性、周波数特性