Evaluation of Subsurface Fatigue Crack Life in Forged Ti-6Al-4V Alloys at Cryogenic Temperatures
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue crack growth modeling was performed for Ti–6Al–4V forged materials failed by subsurface crack generation at cryogenic temperatures. The modeling that was based on linear fracture mechanics under the Mode I condition provided a good estimate of the stress intensity range of subsurface or surface and fatigue crack growth, enabling the estimation of the crack propagation life. The fatigue crack growth rate calculated using the Paris rule, da/dN=C(ΔKI)m, almost corresponded to the one obtained from the analysis of the striation on the fracture surface. The calculated crack propagation life was less than a tenth of the number of cycles to failure over 106. As a result, the subsurface crack initiation (Stage I crack generation) process consumed a large number of cycles to failure—as many as that at a lower stress level.
- 社団法人 日本鉄鋼協会の論文
- 2009-01-15
著者
-
Umezawa Osamu
Department Of Mechanical Engineering And Materials Science Yokohama National University
-
Umezawa Osamu
Department Of Materials Science And Engineering Graduate School Of Engineering Yokohama National Uni
-
Umezawa Osamu
Department Of Materials Science And Engineering Faculty Of Engineering Yokohama National University
-
HAMADA Makiko
Department of Materials Science and Engineering, Graduate School of Engineering, Yokohama National U
-
Hamada Makiko
Department Of Materials Science And Engineering Graduate School Of Engineering Yokohama National Uni
関連論文
- The fiber components in the biaxially warm-deformed low-carbon steels
- Analysis of the dislocation structure in warm - deformed steels by the modified Warren - Averbach X - ray profile method
- Improvement of strength-and-toughness balance of recycled steel through ultrarefinement of grain size
- Analysis on Refinement of Columnar γ Grain by Phosphorus in Continuously Cast 0.1mass% Carbon Steel
- Influence of Phosphorus on Solidification Structure in Continuously Cast 0.1mass% Carbon Steel
- 低炭素鋼CC材の柱状γ粒におけるPによる微細化効果
- 高P含有低炭素鋼CC材の組織に及ぼす凝固モードの影響
- Structure of Continuously Cast Slab of High Phosphorus 0.1mass%C Steel
- EVALUATION OF FLOATING DUST CONCENTRATIONS GENERATED FROM DROPPED TEST MATERIALS BY DIGITAL DUST INDICATOR
- Continuously cast 0.1wt% C steels with high phosphorus : microstructural design and control
- Continuously Cast 0.1 mass pct. C Steele with High Phosphorus: Microstructural Design and Control
- Continuously Cast 0.1 mass pct. C Steels with High Phosphorus : Microstructural Design and Control
- Continuously Cast 0.1 mass pct. C Steels with High Phosphorus: Microstructural Design and Control
- Subsurface Fatigue Crack Generation and Strain Incompatibility Near Grain Boundaries for a Nitrogen-strengthened Austenitic Steel at Cryogenic Temperatures
- Evaluation of Subsurface Fatigue Crack Life in Forged Ti-6Al-4V Alloys at Cryogenic Temperatures
- Influence of Phosphorus Micro-Segregation on Ferrite Structure in Cast Strips of 0.1mass% C Steel
- Microstructure of Cast Strip in 0.1mass%C Steels Containing Phosphorus
- PREFACE
- Fatigue Properties of Titanium Alloys in Liquid Helium
- SPECIES DIFFERENCES IN DISPOSITION OF CARBAMAZEPINE AND ITS EPOXIDE METABOLITE
- PHARMACOKINETIC STUDY OF CARBAMAZEPINE AND ITS EPOXIDE METABOLITE IN HUMANS
- EVALUATION OF CARBAMAZEPINE PREPARATIONS : BIOAVAILABILITY AND PHARMACOKINETICS OF CARBAMAZEPINE AND ITS EPOXIDE IN HUMAN
- Special Issue on Growth of Ecomaterials as a Key to Eco-Society III
- Distribution of Internal Crack Initiation Sites in High-cycle Fatigue for Titanium Alloys
- Slip Deformation Analysis Based on Full Constraints Model for α-Titanium Alloy at Low Temperature
- Internal crack initiation in high-cycle fatigue of a Ti-Fe-O alloy at liquid nitrogen temperature
- Hot extrusion for Al-Si-(Fe, Cu) hyper-eutectic cast alloys
- Internal crack initiation in high cycle fatigue of Ti-6Al-4V alloys at cryogenic temperatures