Evaporation Behavior of Zinc Chloride in Ar-O_2-H_2O Atmosphere
スポンサーリンク
概要
- 論文の詳細を見る
Evaporation behavior of ZnCl2 melts and ZnCl2–ZnO mixtures in Ar–O2–H2O atmosphere was observed at 873 K by measuring change of weight and chemical composition. When water vapor or oxygen was added, weight loss of ZnCl2 decreased, and the effect of water vapor on repression of weight loss was much stronger than that of oxygen. Especially, weight loss stagnated after 20 min at 40% of weight loss in Ar–5%H2O atmosphere. It is considered that the reaction product between zinc chloride and water vapor covered the surface of melt.In the case of ZnCl2–ZnO melt, weight loss reached and stagnated at about 60% of initial weight in Ar and Ar–O2 atmospheres. This value is close to initial ZnCl2 content. However, weight loss reached and stagnated at about 50% of initial weight in Ar–H2O atmosphere, and the residue was converted to zinc oxide after 60 min experiments. From these results, formation of zinc oxide by the reaction between zinc chloride and water vapor in Ar–H2O atmosphere was confirmed. It is concluded that zinc oxide formed by the reaction on surface of melt prevented the contact between zinc chloride and gas phase, and the evaporation of zinc chloride. This phenomenon caused the stagnation of weight loss with atmosphere containing water vapor.
- 社団法人 日本鉄鋼協会の論文
- 2009-01-15
著者
-
Tsukihashi Fumitaka
Graduate School of Frontier Sciences, The University of Tokyo
-
Matsuura Hiroyuki
Dep. Of Advanced Materials Sci. Graduate School Of Frontier Sciences The Univ. Of Tokyo
-
Tsukihashi Fumitaka
Department Of Advanced Materials Science Graduate School Of Frontier Sciences The University Of Toky
-
Tsukihashi Fumitaka
Graduate School Of Frontier Sciences The University Of Tokyo
-
YAJIMA Kohei
Graduate School of Frontier Sciences, The University of Tokyo
-
MATSUURA Hiroyuki
Graduate School of Frontier Sciences, The University of Tokyo
-
Yajima Kohei
Department Of Advanced Materials Science Graduate School Of Frontier Sciences The University Of Toky
-
Yajima Kohei
Graduate School Of Frontier Science The University Of Tokyo
-
Matsuura Hiroyuki
Graduate School Of Frontier Sciences The University Of Tokyo
-
Tsukihashi Fumitaka
Graduate School Of Frontier Sciences The Univ. Of Tokyo
-
Tsukihashi Fumitaka
Department Of Advanced Materials Science Graduate School Of Frontier Sciences The University Of Toky
-
Tsukihashi Fumitaka
Graduate School Of Frontier Science The University Of Tokyo
-
Yajima Kohei
Graduate Institute Of Ferrous Technology (gift) Pohang University Of Science And Technology (postech)
関連論文
- 1973KにおけるFe-Al-TiO融液中の脱酸挙動
- 1973KにおけるFe-Al-TiO融液中の脱酸挙動
- Analysis of Global Demand for Iron Source by Estimation of In-use Steel Stock
- 10A-D-4 Quantum neuro-System(Room D International session)
- Surface Active Effect of Na_2O on the Rate of CO_2 Dissociation on the Surface of Molten FeO_x-Na_2O and FeO_x-SiO_2-Na_2O Systems
- Wettability and Interfacial Permeability between Prereduced Ilmenite and Molten Pig Iron
- Analysis of Global Demand for Iron Source by Utility of Stock Hypothesis
- Dissolution Behavior of Solid 5CaO・SiO_2・P_2O_5 in CaO-SiO_2-FeO_x Slag
- Condensation of P_2O_5 at the Interface between 2CaO・SiO_2 and CaO-SiO_2-FeO_x-P_2O_5 Slag
- Effect of Simultaneous Addition of Al_2O_3 and MgO on the Liquidus of the CaO-SiO_2-FeO_x System with Various Oxygen Partial Pressures at 1573K
- Reduction Extraction Kinetics of Titania and Iron from an Ilmenite by H_2-Ar Gas Mixtures
- Evaporation Behavior of Zinc Chloride in Ar-O_2-H_2O Atmosphere
- Removal of Antimony from Liquid Copper by Using CuCl-Na_2CO_3 Fluxes at 1423K
- Mechanisms of Oxidation and Vaporization of Antimony from Liquid Copper with CuCl-CaO Fluxes
- The Transient Stages of Inclusion Evolution During Al and/or Ti Additions to Molten Iron
- Chlorination Kinetics of ZnFe_2O_4 with Ar-Cl_2-O_2 Gas
- Removal of Zn and Pb from Fe_2O_3-ZnFe_2O_4-ZnO-PbO Mixture by Selective Chlorination and Evaporation Reactions
- Evaporation Kinetics of the Molten PbCl_2-ZnCl_2 System from 973 to 1073K
- Oxygen Exchange Reaction between CO_2-CO Gas and Molten Oxide Containing Iron Oxide
- Evaporation kinetics of metal chloride in the ZnCl_2-PbCl_2 system
- Rate of Oxygen Exchange Reaction between CO_2-CO Gas and Molten Iron Oxide
- Bifurcations, Problems on Quantum Computation, And Our New Theory of Calculations
- FeCl_2-ZnCl_2系の蒸発速度
- Three-dimensional Compressible Flow Simulation of Top-blown Multiple Jets in Converter
- Reaction Behavior of P_2O_5 at the Interface between Solid 2CaO・SiO_2 and Liquid CaO-SiO_2-FeO_x-P_2O_5 Slags Saturated with Solid 5CaO・SiO_2・P_2O_5 at 1573K
- Modeling of Three-phase Flows and Behavior of Slag/Steel Interface in an Argon Gas Stirred Ladle
- Large Eddy Simulation on Flow Structure in Centrifugal Flow Tundish
- Formation Reaction of Phosphate Compound in Multi Phase Flux at 1573K
- Partition Equilibria of Lead and Antimony between Liquid Copper and MgO Saturated Cu_2O-SiO_2, Cu_2O-CaO and Cu_2O-CaO-SiO_2 Systems
- Reaction Mechanism between Solid CaO and FeO_x-CaO-SiO_2-P_2O_5 Slag at 1 573K
- Chlorination and Evaporation Behaviors of PbO-PbCl_2 System in Ar-Cl_2-O_2 Atmosphere
- Effect of Al_2O_3 and MgO Additions on Liquidus for the CaO-SiO_2-FeO_x System at 1573K
- Kinetics of Zn Removal from ZnO-Fe_2O_3-CaCl_2 System
- Effect of P_2O_5 Addition on the Rate of CO_2 Dissociation on the Surface of Fe_tO-base Molten Oxides
- Effect of Oxygen Partial Pressure on Liquidus for the CaO-SiO_2-FeO_x System at 1573K
- Analysis of Global Demand for Iron Source by Estimation of In-use Steel Stock
- Flow Patterns in Thin Slab Continuous Casting Mold
- Modeling of Circulating Flow in RH Degassing Vessel Water Model Designed for Two-and Multi-legs Operations
- Prediction Model of Global Demand for Iron Source by Utility of Stock Hypothesis : Verification of Predictive Power and Outlook for Demand to 2050
- Wettability of Sn-Zn, Sn-Ag-Cu and Sn-Bi-Cu Alloys on Copper Substrates
- Thermodynamic Calculation of Generation of H2 Gas by Reaction between FeO in Steelmaking Slag and Water Vapor
- Generation Behavior of H2 Gas by Reaction between FeO-containing Slag and H2O–Ar Gas
- Influence of TiO_2 on the Viscous Behavior of Calcium Silicate Melts Containing 17 mass% Al_2O_3 and 10 mass% MgO
- Radiative Heat Transfer Behavior of Mold Fluxes for Casting Low and Medium Carbon Steels
- Data Arrangement and Consideration of Evaluation Standard for Silico-Ferrite of Calcium and Alminum (SFCA) Phase in Sintering Process
- Removal of Copper from Molten Steel using FeO–SiO2–CaCl2 Flux
- Selective Chlorination Reaction of Cu2O and FeO Mixture by CaCl2
- Quantum Circuits and Its Application for Neuro-Junction(INNOVATIVE BIOMEDICAL TECHNOLOGIES and INFORMATICS, BMFSA2008)
- Current, Magnetic Field and Joule Heating in Electroslag Remelting Processes
- Thermodynamic Calculation of Generation of H_2 Gas by Reaction between FeO in Steelmaking Slag and Water Vapor
- Selective Chlorination Reaction of Cu_2O and FeO Mixture by CaCl_2
- Removal of Copper from Molten Steel using Fe0-Si0_2-CaCl_2 Flux