Application of Modified Coke to NO_x Reduction with Recycling Flue Gas during Iron Ore Sintering Process

スポンサーリンク

概要

• 論文の詳細を見る

• A new process, named NOx reduction by the modified coke with recycling flue gas, was proposed. The coke samples loaded with K2CO3, CaO and CeO2 were characterized by SEM. The effects of the recycled flue gas and the modified coke on NOx reduction were investigated with a quartz fixed bed reactor and a sintering pot. The results showed that the extent of the contact between additives and coke was: K2CO3>CaO>CeO2. In the modified coke combustion with recycling flue gas, the concentration of NOx emission was decreased, furthermore, the NOx reduction ratio increased with the loading amount of additives. The NOx reduction ratios were 36.7%, 20.2% and 26.2% respectively when the loading amount of K2CO3, CaO and CeO2 was 2.0%. In sintering pot tests, the coke loaded with 2.0% CeO2 was used as fuel and the recycled flue gas, simulated by the gas mixture with 50 ppm NO, was introduced to sintering process, the NOx reduction ratio was 38.0%, which was about 13% higher than that of the base run with recycling flue gas.

• 社団法人 日本鉄鋼協会の論文
• 2008-11-15

著者

• Chen Yan-guang

  State Key Laboratory Of Multi-phase Complex System Institute Of Process Engineering Chinese Academy

• GUO Zhan-cheng

  State Key Laboratory of Multi-phase Complex System, Institute of Process Engineering, Chinese Academ

• WANG Zhi

  State Key Laboratory of Multi-phase Complex System, Institute of Process Engineering, Chinese Academ

• Guo Zhan-cheng

  State Key Laboratory Of Multi-phase Complex System Institute Of Process Engineering Chinese Academy

• Wang Zhi

  National Engineering Lab. For Hydrometallurgical Cleaner Production Technol. Inst. Of Process Engineering Chinese ...

• Wang Zhi

  State Key Laboratory Of Automotive Safety And Energy Tsinghua University

• Guo Zhan-Cheng

  State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing

関連論文

• Application of Modified Coke to NO_x Reduction with Recycling Flue Gas during Iron Ore Sintering Process
• The Arg194Trp Polymorphism in the X-ray Repair Cross-Complementing Group 1 Gene as a Potential Risk Factor of Oral Cancer : A Meta-Analysis
• Relation between Sticking and Metallic Iron Precipitation on the Surface of Fe_2O_3 Particles Reduced by CO in the Fluidized Bed
• Influence of Temperature on Sticking Behavior of Iron Powder in Fluidized Bed
• OS-C3: Numerical Study of Stratification on HCCI Combustion for Higher Load Extension(OS-C The Role of Heterogeneity of mixture on HCCI and PCCI Combustion,Organized Session Papers)
• Characterization of Precipitated Carbon by XPS and Its Prevention Mechanism of Sticking during Reduction of Fe2O3 Particles in the Fluidized Bed

スポンサーリンク