Formability of C-Si-Mn-Al-Nb-Mo Ultra High-strength TRIP-aided Sheet Steels

概要

論文の詳細を見る
Formable 980–1470 MPa grade ultra high-strength TRIP-aided sheet steels with bainitic ferrite matrix (TBF steels) have been developed for cold forming of automotive applications. Complex additions of 1.0%Al–0.05%Nb–0.2%Mo to 0.2%C–1.5%Si–1.5%Mn base steel increased both the volume fraction and carbon concentration of retained austenite films of the TBF steel, with refining of microstructure. Extremely much retained austenite was realized in the TBF steel austempered at 450–500°C, corresponding to hot-dip galvanization just after annealing. Good combinations of strength and elongation and strength and stretch-flangeability were achieved when the TBF steel was austempered at 450–500°C and 425–475°C, respectively. These good combinations were caused by fine lath structure and a large amount of metastable retained austenite film. It is noteworthy that the TBF steel exhibited an excellent combination of total elongation and stretch-flangeability when austempered at 325–350°C lower than MS.
社団法人日本鉄鋼協会の論文
2007-09-15