Microwave Absorption Behavior of Iron-Alumina Mixed Powder at Elevated Temperature
スポンサーリンク
概要
- 論文の詳細を見る
Recently, it has been reported that metal powders can be heated by microwave irradiation and many attentions have been attracted on the research field. More effectively heating of iron powder in H field than E field has also been reported. From this result, it is supposed that microwave absorbability of iron powder may change at Curie temperature since iron losses magnetism at the temperature. The objective of this work is to reveal the microwave absorption behavior of iron powder around Curie temperature. For this purpose, microwave absorption behavior of iron–alumina mixed powder at elevated temperature was measured by using a circular wave-guide fixture and a microwave vector network analyzer. When iron powder was subjected to a measurement, compact body of iron powder became a reflector for microwave above 700°C, hence any change of absorbability around Curie temperature (780°C) could not be obtained. When iron(50mass%)–alumina(50mass%) powder was subjected to measurement, drastic change of microwave absorbability was observed at Curie temperature. From the absorbability change around Curie temperature, it was estimated that contribution ratios of magnetic loss is 72% and of dielectric loss is 28% on microwave absorbability for iron(50mass%)–alumina(50mass%) mixed powder.
- 社団法人 日本鉄鋼協会の論文
- 2007-04-15
著者
-
SANO Saburo
National Institute of Advanced Industrial Science and Technology
-
Takao Yasumasa
National Institute Of Advanced Industrial Science And Technology 'aist'
-
Takao Yasumasa
National Institute Of Advanced Industrial Science And Technology (aist)
-
Takao Yasumasa
National Industrial Research Institute Of Nagoya
-
Sano Saburo
National Inst. Of Advanced Industrial Sci. And Technol. (aist) Aichi Jpn
-
Sano Saburo
National Institute Of Advanced Industrial Science And Technology (aist)
-
TAKAYAMA Sadatsugu
National Institute of Advanced Industrial Science and Technology (AIST)
-
TSUZUKI Akihiro
National Institute of Advanced Industrial Science and Technology (AIST)
-
MAKINO Yukio
JWRI, Osaka University
-
Makino Yukio
Jwri Osaka University
-
TAKAYAMA Sadatsugu
National Institute for Fusion Science
関連論文
- Densification Behavior and Crystallite Growth in Alumina-YSZ Composites Sintered by Millimeter-wave Heating
- Compositional Effects of Ytterbia-Alumina Additives on Millimeter-Wave Sintering of Silicon Nitride(Physics, Processes, Instruments & Measurements)
- Enhancement for Synthesis of Bi-Pb-Sr-Ca-Cu-O Superconductor by the Spray Drying and Subsequent Calcination with Rapid Heating
- Synthesis of Y-Ba-Cu-O Ultrafine Powders by Spray Drying and Subsequent Calcination under Low Pressure
- Microwave Absorption Behavior of Iron-Alumina Mixed Powder at Elevated Temperature
- Particle Aggregated Structure in Silica Particle Filled Epoxy Resin Composite System
- Microstructure control of an oxide superconductor by a hybridization process through grinding
- Characteristics of Millimeter-wave Heating and Smart Materials Synthesis
- Optical Polarization Technique for Observing Filler Packing-structure in the Ceramic-powder Filled Resin Polymer Composite Systems
- Contribution of particle structure to the viscosity of SiO_2 particle-filled epoxy resin composite systems
- SYNTHESIS AND PROPERTIES OF POWDERED OXIDE SUPERCONDUCTOR BY THE MIST PYROLYSIS METHOD
- Microwave-energy Distribution for Reduction and Decrystallization of Titanium Oxides
- Effect of H-field or E-field on Sintering and Decrystallization of Titanium Oxides during 2.45GHz Microwave Heating
- Interaction of Microwaves with Synthetic Type A Zeolite Containing Water
- Interaction of Microwaves with Synthetic Type A Zeolite Containing Water (Special Issue : Advanced Plasma Science and Its Applications for Nitrides and Nanomaterials)
- Microwave Frequency Effect for Reduction of Magnetite
- Investigation of the Microwave Iron-Production Process with Multipoint Pyrometric and Spectroscopic Measurements