Evaluation of the Hot Corrosion Behavior of LPG Assisted HVOF NiCr Wire Sprayed Boiler Tube Steels in Molten Salt Environments

スポンサーリンク

概要

• 論文の詳細を見る

• NiCr coatings were deposited on some boiler tube steels by High Velocity Oxy Fuel spraying process using LPG as fuel gas. Hot corrosion behaviour of uncoated as well as HVOF sprayed specimens was studied in an environment of Na2SO4–60%V2O5 at 900°C under cyclic conditions. The thermogravimetric technique was used to establish the kinetics of corrosion. SEM/EDAX, XRD and EPMA techniques were used to analyse the corrosion products. The NiCr coating found to be very effective in decreasing the corrosion rate of the uncoated steels. The NiCr coated samples showed no cracking or spalling of oxide scale during hot corrosion. The formation of protective oxide scale as observed may be contributing to the development of hot corrosion resistance in the coatings studied, which mainly consists of oxides of NiO, NiCr2O4 and Cr2O3.

• 社団法人 日本鉄鋼協会の論文
• 2006-07-15

著者

• Sidhu Buta

  Department Of Mechanical Engineering G.z.s. College Of Engineering And Technology

• Sidhu Hazoor

  Department Of Mechanical Engineering Yadvindra College Of Engineering Punjabi University Guru Kashi

• PRAKASH S.

  Department of Metallurgical and Materials Engineering, Indian Institute of Technology

• Prakash S.

  Department Of Anatomy Dr. Arcot Lakshmanasamy Mudaliar Postgraduate Institute Of Basic Medical Scien

関連論文

• Anatomical aspects of the male reproductive system in the bonnet monkey (Macaca radiata)
• Evaluation of the Hot Corrosion Behavior of LPG Assisted HVOF NiCr Wire Sprayed Boiler Tube Steels in Molten Salt Environments
• Meteorological influences on the incidence of lichen planus in a north Indian population

スポンサーリンク